Chi Mei Wonderlite® PC-175 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Wonderlite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Wonderlite® PC-175 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Optical Disk
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Melt Flow | 65 g/10 min @Load 1.20 kg, Temperature 300 °C |
65 g/10 min @Load 2.65 lb, Temperature 572 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 106 MPa | 15400 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 65 % | 65 % | 50 mm/min; ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/4A |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | annealed; ISO 75 |
| 140 °C | 284 °F | unannealed; ISO 75 | |
| Vicat Softening Point | 140 °C @Load 5.00 kg |
284 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 145 °C @Load 1.00 kg |
293 °F @Load 2.20 lb |
50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- Raschig Group AMPLA® 2500 melamine-modified polyester
- LG Chemical RS-800 ABS, Extrusion, High Impact, HCFC Resistant
- LATI Later 4 G/30 PBT, 30% Glass Fiber Reinforced
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 150 Gauge
- Arlon 51976R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF Styropor® BF 322 EPS
Copyright © lookpolymers.com All Rights Reserved