Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 70.0 - 180 MPa @Temperature 125 - 275 °C |
10200 - 26100 psi @Temperature 257 - 527 °F |
Average value: 123 MPa Grade Count:1 |
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Carbon Fiber Filled". Each property range of values reported .. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5 mm/min |
Polimeri Europa KOBLEND PCA PD 935 G2 PC+ABS, 10% Glass Fiber
(discontinued **) Symbol according to ISO 1043/1/2: PC+ABS (GF) Injection moulding grade, reinforced with 10% glass fibres, high stiffness, very good dimensional stability. Vicat/B50 = 135°C Main application field.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638-68 |
Budd DSM-971 Smooth Surface, Class "A" SMC
(discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 70.0 - 165 MPa @Temperature 60.0 - 150 °C |
10200 - 23900 psi @Temperature 140 - 302 °F |
Average value: 113 MPa Grade Count:1 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | 70.0 - 310 MPa | 10200 - 45000 psi | Average value: 173 MPa Grade Count:48 |
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 70.0 - 80.0 MPa @Temperature 130 - 175 °C |
10200 - 11600 psi @Temperature 266 - 347 °F |
Average value: 66.6 MPa Grade Count:2 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 70.0 - 80.0 MPa @Time 1.80e+7 - 7.20e+7 sec |
10200 - 11600 psi @Time 5000 - 20000 hour |
Average value: 66.6 MPa Grade Count:2 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 70.0 - 155 MPa @Temperature 60.0 - 150 °C |
10200 - 22500 psi @Temperature 140 - 302 °F |
Average value: 61.4 MPa Grade Count:2 |
Overview of materials for Nylon 610 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
Tensile Strength, Ultimate | 70.0 - 155 MPa @Temperature 60.0 - 150 °C |
10200 - 22500 psi @Temperature 140 - 302 °F |
Average value: 108 MPa Grade Count:2 |
Overview of materials for Nylon 610, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Glass Reinforced". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
ICE Steatite L-5 Data provided by the manufacturer, International Ceramic Engineering. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
Haysite HCR-125 Corrosion Resistant Vinyl Ester/Glass Sheet A fiber glass reinforced thermoset sheet using DEREKANE® 470 vinylester in the resin matrix with flame retardant and ultraviolet inhibitors. Standard color is beige. Derakane® 470 is a registe.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | Safety factor of 10-20X is necessary in practice |
Saint-Gobain Vitreosil® Clear Fused Quartz Tubing Electrically fused quartz is recognized for its combination of purity, chemical inertness, physical stability, thermal shock resistance, high electrical resistivity, and high operating temperatures... |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
Styrolution NOVODUR® P2HGV ABS, 16% Glass Fiber Injection molding grade, glass reinforced (16%).Applications: Automotive industry: instrument panels, rear light housings, internal components of domestic appliances. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Sumitomo Bakelite North America RX® 2-520 Short-Glass Reinforced Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SI.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ISO 527 |
Sumitomo Bakelite North America RX® 660 Fiberglass Reinforced Phenolic Novolac RX 660 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type MFH.Information supplied by Sumitom.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Plenco 00732 Melamine-Phenolic, Granular, Injection Molded PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ISO 527 |
Wellman Wellamid® 22LHI3 XE-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ISO 527 |
Wellman Wellamid® GS40-60 42L-N 40% Glass Sphere Filled Nylon 6, Lubricated Typical Applications: Potentiometer liners, electrical coil forms, automotive window lift and power door lock switch bodies, gears, thick wall section moldings, emission control valves.Data provided.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Tipco Tipcolene® SEB 300 FR - UL94-V-0 Flame Retardant, 10% Chemically Coupled Glass Fiber Polypropylene Homopolymer 30% Glass Reinforced, Flame Retardant PP HomopolymerApplications: Electrical & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1013G15 1 NA PA6-GF15 15% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Cast Nylons Nycast® 6MPY Plasticized Nylon 6 A plasticized Type 6 material, NYCAST® 6MPY is formulated for use as pile driver caps or cushion pads. Data provided by the manufacturer, Cast Nylons Limited.The data below are average values prese.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
BASF Procom® GC20H 250 Polypropylene Uses: car and truck fans and shrouds, car rear light housings, car radiator expansion tanks, car grills, domestic appliance components (e.g. washing machine tanks, impellers housings, etc.), textile.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 112 Polypropylene, Glass Reinforced, Chemically Coupled, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 70.0 - 255 MPa | 10200 - 37000 psi | Average value: 166 MPa Grade Count:88 |
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 70.0 MPa @Temperature 704 °C |
10200 psi @Temperature 1300 °F |
|
AK Steel 439 ULTRA FORM® Stainless Steel AK Steel 439 ULTRA FORM™ was developed for applications requiring oxidation and corrosion resistance superior to Type 409 as well as superior formability to AK Steel 439 Stainless Steel. As a resul.. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5mm/min; ISO 527 |
BASF Ultradur B 4040 G3 HT BK5830 15% Glass Filled PBT/PET Ultradur B 4040 G3 HT BK5830 is a 15% glass filled, pigmented black, injection molding PBT. It is a resin for molding household appliances and equipment which must be resistant to chemicals and oth.. |
|||
Tensile Strength, Ultimate | 70.0 - 95.0 MPa @Temperature 60.0 - 150 °C |
10200 - 13800 psi @Temperature 140 - 302 °F |
Average value: 82.5 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a.. |
|||
Tensile Strength, Ultimate | 70.0 - 175 MPa | 10200 - 25400 psi | Average value: 122 MPa Grade Count:71 |
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 663 Nylon 6, Glass Bead Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
Solvay Specialty Polymers Ixef® 2010/X914 Polyarylamide, 40% Filler, at Equilibrium (65% RH)
(discontinued ** The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A.. |