DSM Novamid® 1013G15 1 NA PA6-GF15
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1013G15 1 NA PA6-GF15.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass Reinforced, Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 3.00 % | 3.00 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | cond; ISO 527-1/-2 |
| 130 MPa | 18900 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.7 % | 2.7 % | dry; ISO 527-1/-2 |
| 8.7 % | 8.7 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 2.80 GPa | 406 ksi | cond; ISO 527-1/-2 |
| 5.80 GPa | 841 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 115 MPa | 16700 psi | cond; ISO 178 |
| 200 MPa | 29000 psi | dry; ISO 178 | |
| Flexural Modulus | 2.90 GPa | 421 ksi | cond; ISO 178 |
| 5.40 GPa | 783 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 3.90 J/cm² @Temperature 23.0 °C |
18.6 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 10.6 J/cm² @Temperature 23.0 °C |
50.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.00e+14 ohm-cm | 6.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 8.00e+13 ohm | 8.00e+13 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
dry; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.023 @Frequency 1.00e+6 Hz |
0.023 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- RheTech Products GC30P200-523 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, (GM 167A) Ebony
- MetalTek AGMA CL A UNS C90800 Gear Bronze
- Teknor Apex Monprene® MP-1698 Thermoplastic Elastomer
- SABIC Innovative Plastics LNP STAT-KON DX95523C PC (Asia Pacific)
- Polyram Bondyram® 1010 Maleic Anhydride Modified Polypropylene
- Hexcel® HexPly® 954-6 Curing Cyanate Resin, M55J Fiber
- ExxonMobil Bicor® 110 ASB-X OPP Film
- Polykemi AB POLYfill PPHC K8030 Polypropylene, Mineral Reinforced
- LNP ULTEM® SMU5852 Polyetherimide, 30% Carbon Fiber Reinforcement, 15% PTFE Lubricant (discontinued **)
Copyright © lookpolymers.com All Rights Reserved