Polymer Property : Tensile Strength, Ultimate = 10200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	70.3 MPa	10200 psi	ASTM D638-95
Multibase Multi-Pro® 4008 RC Medium Impact 40% Glass Filled Polypropylene Multi-Pro 4008 RC is a chemically coupled glass reinforced polypropylene compound exhibiting highest flexural modulus, flex strength and high impact resistance. Heat resistance is high due to highl..
Tensile Strength, Ultimate	70.3 MPa	10200 psi	ASTM D638
Nylene® 4214-15 (HS) , 15% Glass Fiber Reinforced Impact Modified Nylon 6 Description: Nylene® 4214-15 (HS) is a 15% glass filled, high impact nylon 6. Information provided by Custom Resins.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Res..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM data at 5 mm/min.
BASF Capron® GR15 HS 15% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron GR15 HS is a heat stabilized 15% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aest..
Tensile Strength, Ultimate	70.0 MPa @Temperature 90.0 °C	10200 psi @Temperature 194 °F	ISO 527
LATI LARIL 13 G/20-V1 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM D638-68
Budd DSM-971 Smooth Surface, Class "A" SMC (discontinued **) Parts requiring high strength and dimensional stability, excellent surface smoothness without sink marks; parts to be painted requiring an automotive-type finish.Data provided by the manufacturer.
Tensile Strength, Ultimate	70.0 - 165 MPa @Temperature 60.0 - 150 °C	10200 - 23900 psi @Temperature 140 - 302 °F	Average value: 113 MPa Grade Count:1
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Tensile Strength, Ultimate	70.0 - 310 MPa	10200 - 45000 psi	Average value: 173 MPa Grade Count:48
Overview of materials for Nylon 6, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of a..
Tensile Strength, Ultimate	70.0 - 80.0 MPa @Time 1.80e+7 - 7.20e+7 sec	10200 - 11600 psi @Time 5000 - 20000 hour	Average value: 66.6 MPa Grade Count:2
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. ..
Tensile Strength, Ultimate	70.3 MPa	10200 psi	ASTM D638
Global 120-PC-Natural Acrylonitrile Styrene, General Purpose Grade Description-transparent, natural, medium impact resistance, high hardness, high heat resistance, good chemical resistanceApplications-automotive, electrical parts, household goodsInformation provide..
Tensile Strength, Ultimate	70.3 MPa	10200 psi	ASTM D638
Global 121-PC-Blue Acrylonitrile Styrene, General Purpose Grade Description-transparent, blue, medium impact resistance, high hardness, good stiffness, high heat resistance, good chemical resistanceApplications-automotive, electrical parts, household goodsInform..
Tensile Strength, Ultimate	70.0 MPa	10200 psi
ICE Steatite L-4 Data provided by the manufacturer, International Ceramic Engineering.
Tensile Strength, Ultimate	70.0 MPa	10200 psi
ICE Steatite L-5 Data provided by the manufacturer, International Ceramic Engineering.
Tensile Strength, Ultimate	70.0 MPa	10200 psi	5 mm/min; ISO 527
Lucite International Perspexâ„¢ XT Acrylic Extruded Sheet 0X00 PERSPEX extruded sheet has a lower molecular weight making it easy to vacuum form and the extrusion process gives excellent thickness tolerance and is economical for long production runs.Information..
Tensile Strength, Ultimate	70.0 MPa	10200 psi
Haysite HCR-125 Corrosion Resistant Vinyl Ester/Glass Sheet A fiber glass reinforced thermoset sheet using DEREKANEÂ® 470 vinylester in the resin matrix with flame retardant and ultraviolet inhibitors. Standard color is beige. DerakaneÂ® 470 is a registe..
Tensile Strength, Ultimate	70.0 MPa	10200 psi
Haysite HCR-196 Corrosion Resistant Vinyl Ester/Glass Sheet A fiber glass reinforced thermoset sheet using DEREKANEÂ® 470 vinylester in the resin matrix. Standard color is grey. Additional data covering resistance to specific chemicals is available upon re..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	Safety factor of 10-20X is necessary in practice
Saint-Gobain VitreosilÂ® Clear Fused Quartz Tubing Electrically fused quartz is recognized for its combination of purity, chemical inertness, physical stability, thermal shock resistance, high electrical resistivity, and high operating temperatures...
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM D638
Sumitomo Bakelite North America RXÂ® 2-520 Short-Glass Reinforced Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SI..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM D638
Plenco 00732 Melamine-Phenolic, Granular, Injection Molded PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ISO 527
Wellman Wellamid® GS40-60 42LH-N 40% Glass Sphere Filled Nylon 6, Lubricated & Heat Stabilized Typical Applications: Potentiometer liners, electrical coil forms, automotive window lift and power door lock switch bodies, gears, thick wall section moldings, emission control valves.Data provided..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM D638
Tipco Tipcolene® SEB 300 FR - UL94-V-0 Flame Retardant, 10% Chemically Coupled Glass Fiber Polypropylene Homopolymer 30% Glass Reinforced, Flame Retardant PP HomopolymerApplications: Electrical & AppliancesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Tensile Strength, Ultimate	70.0 MPa	10200 psi	cond; ISO 527-1/-2
DSM Akulon® K224-G3-FC NA99001 PA6-GF15 15% Glass Reinforced
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM D638
Cast Nylons Nycast® 6MPY Plasticized Nylon 6 A plasticized Type 6 material, NYCAST® 6MPY is formulated for use as pile driver caps or cushion pads. Data provided by the manufacturer, Cast Nylons Limited.The data below are average values prese..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	5mm/min; ISO 527
BASF Ultradur B 4040 G3 HT BK5830 15% Glass Filled PBT/PET Ultradur B 4040 G3 HT BK5830 is a 15% glass filled, pigmented black, injection molding PBT. It is a resin for molding household appliances and equipment which must be resistant to chemicals and oth..
Tensile Strength, Ultimate	70.0 - 175 MPa	10200 - 25400 psi	Average value: 122 MPa Grade Count:71
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of ..
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 663 Nylon 6, Glass Bead Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	70.0 - 100 MPa @Temperature -40.0 - -40.0 °C	10200 - 14500 psi @Temperature -40.0 - -40.0 °F	Average value: 85.0 MPa Grade Count:4
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri..
Tensile Strength, Ultimate	70.0 - 165 MPa	10200 - 24000 psi	Average value: 123 MPa Grade Count:38
Overview of materials for Polybutylene Terephthalate (PBT), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Fiber Filled". Each property range of values reported is minimu..