Styrolution NOVODUR® P2HGV ABS, 16% Glass Fiber
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution NOVODUR® P2HGV ABS, 16% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding grade, glass reinforced (16%).Applications: Automotive industry: instrument panels, rear light housings, internal components of domestic appliances.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | Saturation in water |
| Water Absorption at Saturation | 0.30 % | 0.30 % | |
| Melt Flow | 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Tensile Modulus | 5.50 GPa | 798 ksi | |
| Charpy Impact Unnotched | 1.90 J/cm² | 9.04 ft-lb/in² | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C @Temperature 20.0 °C |
30.0 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Vicat Softening Point | 104 °C | 219 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
|
| 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | |
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
|
| 0.0060 @Frequency 1e+6 Hz |
0.0060 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 575 V | 575 V |
Users viewing this material also viewed the following:
- Iran Petrochemical (PCC) TG 641 Super Bright Polyethylene Terephthalate
- Sekisui PIOCELAN TOPF-40DUB Black (Low VOC, Low odor) Flame Retardant Moldable Polymer Foam
- Teknor Apex Flexalloy® 9900-60 Polyvinyl Chloride Elastomer
- Total PPH 10099 Polypropylene, Homopolymer
- ExxonMobil Mobilith AW Series 00
- Dow Nordel® IP 4770P EPDM Hydrocarbon Rubber
- Eurotec® Tecomid® NB40 NL E PA6, unfilled, natural
- Kazanorgsintez 108-76 Film Grade Composition of High Density Polyethylene
- Unifrax Fiberfrax® Moist Pak-D® Ceramic Fiber Insulator
Copyright © lookpolymers.com All Rights Reserved