Ashley Polymers Ashlene® 851 Nylon 6, High Viscosity
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 851 Nylon 6, High Viscosity.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High viscosity for blown film, tubing, rods and shapes and blow molding. Has highest puncture resistance and clarity. FDA and NSF approved.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Water Absorption | 1.7 % | 1.7 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ATSM D638 |
| Elongation at Yield | 140 % | 140 % | ASTM D638 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 8.00e+13 ohm-cm | 8.00e+13 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 241S PC (Asia Pacific)
- Lanxess Pocan® B 3217 XF 000000 PBT, 16% Glass Fiber
- A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene
- Formosa Plastics Formolene® 5143H Homopolymer Polypropylene
- Arkema Group Orgalloy® LE 60 ES Polyamide Alloy
- Arlon 51599R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 45% Cold Reduction + Aged 538°C (1000°F)/4hr/AC
- Bulk Molding Compounds BMC 665 Mineral filled, 20% glass reinforced polyester molding compound
- Asahi Kasei Thermylene® P6-30FG-0640 30% Glass Fiber Reinforced, Heat and Copper
- Lucobit Lucopren® 1500H Soft Polyolefin Granules
Copyright © lookpolymers.com All Rights Reserved