Ineos ABS Triax® 1315 GF ABS + Polyamide Blend (Conditioned)
| Category | Polymer , Thermoplastic , ABS Polymer , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® 1315 GF ABS + Polyamide Blend (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:Contains FillerSuitable processing methods:Injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.995 g/cc | 0.0359 lb/in³ | Melt |
| 1.17 g/cc | 0.0423 lb/in³ | (DAM) | |
| Water Absorption | 3.8 % | 3.8 % | (from DAM) |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 23°C/50% R.H. (from DAM) |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0035 cm/cm | 0.0035 in/in | |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | |
| Elongation at Break | 5.0 % | 5.0 % | |
| Tensile Modulus | 4.00 GPa | 580 ksi | |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | |
| 3.60 J/cm² @Temperature -30.0 °C |
17.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
DAM |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 20.0 °C |
66.7 µin/in-°F @Temperature 68.0 °F |
DAM |
| Specific Heat Capacity | 1.94 J/g-°C | 0.464 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.155 W/m-K | 1.08 BTU-in/hr-ft²-°F | Melt |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | (from DAM) |
| Vicat Softening Point | 112 °C | 234 °F | 50°C/h 50N (from DAM) |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
|
| 7.9 @Frequency 100 Hz |
7.9 @Frequency 100 Hz |
||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | |
| Dissipation Factor | 0.070 @Frequency 1e+6 Hz |
0.070 @Frequency 1e+6 Hz |
|
| 0.11 @Frequency 100 Hz |
0.11 @Frequency 100 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding |
| Ejection Temperature | 105 °C | 221 °F | |
| Injection Velocity | 40.0 mm/sec | 1.57 in/sec |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Effective thermal diffusivity | 0.801E-7 m²/s | Melt |
Users viewing this material also viewed the following:
- Polymer Resources PC/ABS-FR1-[color]-3 PC Blend, Flame Retardant, Standard Flow, UV Stabilized
- Polymer Resources TP-FR-IM-[color]-3 Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low Flow
- SABIC Innovative Plastics Lexan® FL900 PC
- Eastman 5254 LDPE 4% VA Copolymer, High Clarity, High Impact Film Resin for Laminations (discontinued **)
- Kraton® D1116 (SB)n Branched Copolymer
- Master Bond UV25 One component, moderate viscosity UV curable system
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with Butyl Oleate
- 3M Dyneon™ PFA 6502 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules
- Arlon 43191R012 0.012" (0.305 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved