Solvay Specialty Polymers Ixef® 2010/X914 Polyarylamide, 40% Filler, at Equilibrium (65% RH) (discontinued **

Category	Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Ixef® 2010/X914 Polyarylamide, 40% Filler, at Equilibrium (65% RH) (discontinued **.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay Advanced Polymers.

Physical Properties	Metric	English	Comments
Density	1.58 g/cc	0.0571 lb/in³	Dry as molded

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	70.0 MPa	10200 psi	ASTM D638
Elongation at Break	1.6 %	1.6 %	ASTM D638
Tensile Modulus	6.50 GPa	943 ksi	ASTM D638
Flexural Yield Strength	120 MPa	17400 psi	ASTM D790
Flexural Modulus	5.50 GPa	798 ksi	ASTM D790
Izod Impact, Notched	0.350 J/cm	0.656 ft-lb/in	ASTM D256
Izod Impact, Unnotched	2.50 J/cm	4.68 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	240 °C	464 °F

Processing Properties	Metric	English	Comments
Feed Temperature	250 - 280 °C	482 - 536 °F
Rear Barrel Temperature	250 - 280 °C	482 - 536 °F	Compression Zone
Middle Barrel Temperature	250 - 280 °C	482 - 536 °F	Homogenization Zone
Front Barrel Temperature	260 - 290 °C	500 - 554 °F	Nozzle Zone
Melt Temperature	280 °C	536 °F
Mold Temperature	120 - 140 °C	248 - 284 °F	Needed to develop high crystallinity
Injection Pressure	50.0 - 250 MPa	7250 - 36300 psi
Hold Pressure	30.0 - 150 MPa	4350 - 21800 psi
Back Pressure	0.000 - 1.00 MPa	0.000 - 145 psi