Overview of materials for PBT + PET Blend, Glass Filled

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for PBT + PET Blend, Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.36 - 1.76 g/cc
0.0493 - 0.0636 lb/in³
Average value: 1.56 g/cc Grade Count:77
Filler Content 15.0 - 30.0 %
15.0 - 30.0 %
Average value: 22.5 % Grade Count:4
Water Absorption 0.0300 - 0.400 %
0.0300 - 0.400 %
Average value: 0.327 % Grade Count:23
Moisture Absorption at Equilibrium 0.0300 - 0.200 %
0.0300 - 0.200 %
Average value: 0.120 % Grade Count:47
Water Absorption at Saturation 0.150 - 0.500 %
0.150 - 0.500 %
Average value: 0.242 % Grade Count:20
Viscosity 145000 - 195000 cP
145000 - 195000 cP
Average value: 164000 cP Grade Count:4
12500 - 1.75e+6 cP

@Temperature 230 - 270 °C
12500 - 1.75e+6 cP

@Temperature 446 - 518 °F
Average value: 437000 cP Grade Count:2
12500 - 1.75e+6 cP

@Shear Rate 1.00 - 100000 1/s
12500 - 1.75e+6 cP

@Shear Rate 1.00 - 100000 1/s
Average value: 437000 cP Grade Count:2
Viscosity Test 50.0 - 95.0 cm³/g
50.0 - 95.0 cm³/g
Average value: 80.9 cm³/g Grade Count:16
Maximum Moisture Content 0.0200
0.0200
Average value: 0.0200 Grade Count:5
Linear Mold Shrinkage 0.00100 - 0.0110 cm/cm
0.00100 - 0.0110 in/in
Average value: 0.00430 cm/cm Grade Count:51
Linear Mold Shrinkage, Transverse 0.00100 - 0.0120 cm/cm
0.00100 - 0.0120 in/in
Average value: 0.00697 cm/cm Grade Count:37
Melt Flow 5.00 - 130 g/10 min
5.00 - 130 g/10 min
Average value: 28.1 g/10 min Grade Count:50
Ash 15.0 - 45.0 %
15.0 - 45.0 %
Average value: 30.0 % Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110 - 121
110 - 121
Average value: 118 Grade Count:11
Hardness, H358/30 101 - 234 MPa
14600 - 33900 psi
Average value: 142 MPa Grade Count:10
Ball Indentation Hardness 180 - 250 MPa
26100 - 36300 psi
Average value: 205 MPa Grade Count:4
Tensile Strength, Ultimate 70.0 - 175 MPa
10200 - 25400 psi
Average value: 122 MPa Grade Count:71
Tensile Strength, Yield 75.0 - 175 MPa
10900 - 25400 psi
Average value: 117 MPa Grade Count:25
Elongation at Break 1.10 - 90.0 %
1.10 - 90.0 %
Average value: 3.46 % Grade Count:69
Elongation at Yield 1.00 - 3.00 %
1.00 - 3.00 %
Average value: 2.37 % Grade Count:20
Modulus of Elasticity 5.00 - 19.0 GPa
725 - 2760 ksi
Average value: 10.2 GPa Grade Count:63
Flexural Yield Strength 110 - 260 MPa
16000 - 37700 psi
Average value: 177 MPa Grade Count:43
Flexural Modulus 4.12 - 16.2 GPa
597 - 2350 ksi
Average value: 8.50 GPa Grade Count:44
Izod Impact, Notched 0.350 - 1.08 J/cm
0.656 - 2.02 ft-lb/in
Average value: 0.713 J/cm Grade Count:32
0.300 - 0.850 J/cm

@Temperature -30.0 - 0.000 °C
0.562 - 1.59 ft-lb/in

@Temperature -22.0 - 32.0 °F
Average value: 0.547 J/cm Grade Count:13
Izod Impact, Unnotched 2.50 - 8.27 J/cm
4.68 - 15.5 ft-lb/in
Average value: 5.56 J/cm Grade Count:15
2.80 - 7.45 J/cm

@Temperature -30.0 - -30.0 °C
5.25 - 14.0 ft-lb/in

@Temperature -22.0 - -22.0 °F
Average value: 4.67 J/cm Grade Count:8
Izod Impact, Notched (ISO) 4.00 - 11.0 kJ/m²
1.90 - 5.23 ft-lb/in²
Average value: 8.26 kJ/m² Grade Count:31
4.00 - 10.0 kJ/m²

@Temperature -40.0 - 0.000 °C
1.90 - 4.76 ft-lb/in²

@Temperature -40.0 - 32.0 °F
Average value: 7.70 kJ/m² Grade Count:29
Izod Impact, Unnotched (ISO) 22.0 - 65.0 kJ/m²
10.5 - 30.9 ft-lb/in²
Average value: 39.9 kJ/m² Grade Count:23
20.0 - 60.0 kJ/m²

@Temperature -30.0 - -30.0 °C
9.52 - 28.6 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 38.7 kJ/m² Grade Count:21
Charpy Impact Unnotched 2.30 - 7.00 J/cm²
10.9 - 33.3 ft-lb/in²
Average value: 4.54 J/cm² Grade Count:41
2.00 - 7.00 J/cm²

@Temperature -30.0 - -30.0 °C
9.52 - 33.3 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 4.27 J/cm² Grade Count:34
Charpy Impact, Notched 0.380 - 2.30 J/cm²
1.81 - 10.9 ft-lb/in²
Average value: 0.890 J/cm² Grade Count:46
0.400 - 1.20 J/cm²

@Temperature -30.0 - -20.0 °C
1.90 - 5.71 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.897 J/cm² Grade Count:30
Dart Drop, Total Energy 5.00 - 8.00 J
3.69 - 5.90 ft-lb
Average value: 6.79 J Grade Count:14
Puncture Energy 2.10 - 3.50 J
1.55 - 2.58 ft-lb
Average value: 2.50 J Grade Count:5
1.80 - 1.80 J

@Temperature -30.0 - -30.0 °C
1.33 - 1.33 ft-lb

@Temperature -22.0 - -22.0 °F
Average value: 1.80 J Grade Count:1
Tensile Creep Modulus, 1 hour 7200 - 16500 MPa
1.04e+6 - 2.39e+6 psi
Average value: 11700 MPa Grade Count:8
Tensile Creep Modulus, 1000 hours 6100 - 15000 MPa
885000 - 2.18e+6 psi
Average value: 10300 MPa Grade Count:8
Taber Abrasion, mg/1000 Cycles 17.0 - 45.0
17.0 - 45.0
Average value: 30.3 Grade Count:6
Thermal Properties Metric English Comments
CTE, linear 2.00 - 55.0 µm/m-°C
1.11 - 30.6 µin/in-°F
Average value: 28.7 µm/m-°C Grade Count:46
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 - 2.00e+20 ohm-cm
1.00e+13 - 2.00e+20 ohm-cm
Average value: 1.03e+19 ohm-cm Grade Count:37
Surface Resistance 1.00e+13 - 5.40e+16 ohm
1.00e+13 - 5.40e+16 ohm
Average value: 4.62e+15 ohm Grade Count:30
Dielectric Constant 2.90 - 4.70
2.90 - 4.70
Average value: 3.79 Grade Count:31
Dielectric Strength 8.00 - 38.0 kV/mm
203 - 965 kV/in
Average value: 23.8 kV/mm Grade Count:27
Dissipation Factor 0.000800 - 0.0200
0.000800 - 0.0200
Average value: 0.00847 Grade Count:29
Arc Resistance 60.0 - 180 sec
60.0 - 180 sec
Average value: 110 sec Grade Count:3
Comparative Tracking Index 175 - 600 V
175 - 600 V
Average value: 275 V Grade Count:38
Hot Wire Ignition, HWI 60.0 - 120 sec
60.0 - 120 sec
Average value: 108 sec Grade Count:5
High Amp Arc Ignition, HAI 15.0 - 120 arcs
15.0 - 120 arcs
Average value: 81.0 arcs Grade Count:5
High Voltage Arc-Tracking Rate, HVTR 150 mm/min
5.91 in/min
Average value: 150 mm/min Grade Count:3