- Samyang Trirex® 3025GRU10 Polycarbonate, 10% Glass Reinforced
Samyang Trirex® 3025GRU10 Polycarbonate, 10% Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3025GRU10 Polycarbonate, 10% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries.Characteristics:10% milled glass fiberApplications:Particularly suitable for camera parts.All information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Water Absorption | 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 58.8 MPa | 8530 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | ASTM D790 |
| Izod Impact, Unnotched | 0.785 J/cm @Thickness 3.17 mm |
1.47 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.0 µm/m-°C | 23.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.97 @Frequency 1.00e+6 Hz |
2.97 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | ASTM D149 |
| Dissipation Factor | 0.0096 @Frequency 1.00e+6 Hz |
0.0096 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Middle Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Melt Temperature | 300 - 310 °C | 572 - 590 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS (Europe-Africa-Middle East)
- ExxonMobil Escorene® LD-325 EVA Film Resin, High Clarity, High Impact (discontinued **)
- Less Common Metals Tb-Fe-Co Cast Magneto-Optic Alloy
- Lubriplate FB 150L USP Mineral Oil-Based Food Machinery Grade Oil
- A. Schulman PAPERMATCH® T-4228-8 Specialty Masterbatch
- Hexcel® HexPly® 954-3 Curing Cyanate Resin, YSH-60A Fiber
- Carmel Olefins CAPILENE® T 77 A Polypropylene Homopolymer
- Bhansali Engineering Abstron AN450M Flame Retardant ABS
- Industeel SUPERELSO® 890 HLE Steel for Welded and Weight-Saving Structures
Copyright © lookpolymers.com All Rights Reserved