LG Chemical LUCON CP6062EX PC/ABS+CNT
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | LG Chemical LUCON CP6062EX PC/ABS+CNT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Sheet Extrusion or Injection Molding, PC/ABS+CNT, Electrostatic Dissipation, Wide Processing Range, Low Surface ResistivityApplication: BLU Carrying TrayCAS No. 103598-77-2, 9003-56-9, 1333-86-4 and 7782-42-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0050 - 0.0070 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min <br>@Load 2.16 kg,<br> Temperature 300 °C |
20 g/10 min <br>@Load 4.76 lb,<br> Temperature 572 °F |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.8 MPa <br>@Thickness 3.20 mm |
8530 psi <br>@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 14 % <br>@Thickness 3.20 mm |
>= 14 % <br>@Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa <br>@Thickness 3.20 mm |
14200 psi <br>@Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 2.75 GPa <br>@Thickness 3.20 mm |
398 ksi <br>@Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.343 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
0.643 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C <br>@Thickness 6.40 mm |
230 °F <br>@Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Front Barrel Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 5.00 - 7.00 hour | 5.00 - 7.00 hour | Injection Molding |
| Back Pressure | 0.000 - 1.96 MPa | 0.000 - 284 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6806 Adhesive
- Kolon KOPA® KN133G33HIBL G/F Reinforced Nylon 6
- Lubriplate Flush Pure USP Mineral Oil-Based Food Machinery Grade Oil
- Karina 18/91-RG-GE (CS) Gray Color Concentrate
- SABIC Innovative Plastics NORYL PX0844 PPE+PS (Asia Pacific)
- Wanhua Chemical Wanthane® WHT-1685AD Polyester Based TPU
- CMW® ELKONIUM 217 Silver Cadmium Alloy
- PolyOne Synprene® IT 38-096 Thermoplastic Elastomer - SBC (discontinued **)
- DuPont Bexloy® AXW604BK 3% Glass Reinforced, Heat Stabilized Modified Ionomer Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved