LG Chemical LUCON PS4200 ABS+CF
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON PS4200 ABS+CF.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, ABS+CF, Electrostatic Dissipation, Good Dimensional Stability, Low WarpageApplication: IC TrayCAS No. 9003-56-9, 12001-26-2 and 7440-44-0Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 0.35 % @Temperature 23.0 °C, Time 86400 sec |
0.35 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength, Yield | 64.7 MPa @Thickness 3.20 mm |
9390 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 10 % @Thickness 3.20 mm |
>= 10 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 5.39 GPa @Thickness 3.20 mm |
782 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.490 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 0.918 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1e+05 - 1.00e+9 ohm | 1e+05 - 1.00e+9 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Middle Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Front Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Nozzle Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.000 - 3.92 MPa | 0.000 - 569 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polymer Resources PPX/NY G10 PPO/Nylon 66 Alloy , 10% Glass Reinforced
- Polymer Resources NY66-G13-[color]-H Nylon 66, 13% Glass Reinforced, Heat Stabilized
- Kingfa HR-528 Modified ABS
- SSAB Tunnplat Aluzink B500A Metal-coated Mild Steel
- A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin
- A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy
- Eurostar Staramide BG6H PA6, 30% Glass Filled, Injection Molded
- Borealis Visico™ LE4423/LE4460/LE4432 Scorch Retardant, Moisture-Crosslinking Polyethylene Compound for Low Voltage Installation
- Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved