LG Chemical LUPOY GN5001RFP PC/ABS, Halogen Free Flame Retardant, Heat Resistance
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GN5001RFP PC/ABS, Halogen Free Flame Retardant, Heat Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, General PurposeApplication: E&E (TV, Navigation Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.7 MPa @Thickness 3.20 mm |
9530 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 80 % @Thickness 3.20 mm |
80 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.75 GPa @Thickness 3.20 mm |
398 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.20 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | |
| UL RTI, Mechanical without Impact | 85.0 °C | 185 °F | |
| Flammability, UL94 | V-0 @Thickness >=1.20 mm |
V-0 @Thickness >=0.0472 in |
|
| V-0 @Thickness >=2.50 mm |
V-0 @Thickness >=0.0984 in |
||
| V-0 @Thickness >=3.00 mm |
V-0 @Thickness >=0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 265 °C | 464 - 509 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Injection Molding |
| Front Barrel Temperature | 255 - 275 °C | 491 - 527 °F | Injection Molding |
| Nozzle Temperature | 260 - 280 °C | 500 - 536 °F | Injection Molding |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | Injection Molding |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection Molding |
| Drying Temperature | 85.0 - 95.0 °C | 185 - 203 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.00200 - 0.00600 MPa | 0.290 - 0.870 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Nye Lubricants 885 (FG) Synthetic Oil
- Palm Labs Adhesives Turbo Anti-Seize Copper Paste
- DSM Arnite® CCT GF30 (T-X01301) PBT-30% Glass Reinforced (European Grade) (discontinued **)
- Reliance Industries Repol B120MA Polypropylene
- KB Alloys 1% Beryllium Aluminum Alloy
- Lehmann & Voss LUVOCOM® NSB 90 NT Polyamide 66, with PTFE
- Fainplast Compounds PH 60/A Flexible PVC, Transparent Extrusion
- Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 1 hr
- Ametek Ultra 304L P/M Stainless Steel, Sintered from 6.2 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved