Kolon KOPA® KN173MC M/F Reinforced Nylon 6

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Kolon
Trade Name Kopa®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kolon KOPA® KN173MC M/F Reinforced Nylon 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubrication and abrasion resistance, excellent chemical resistance, wide usage temperature, good impact absorbing characteristicsInformation provided by US distributor, API-Kolon.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
DIN 53479; ASTM D792
Water Absorption 0.70 %
0.70 %
DIN 53475; ASTM D570
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
DIN 53505; ASTM D785
Tensile Strength, Ultimate 59.8 MPa
8680 psi
DIN 53455; ASTM D638
Elongation at Break 25 %
25 %
DIN 53455; ASTM D638
Flexural Yield Strength 98.1 MPa
14200 psi
DIN 53455; ASTM D790
Flexural Modulus 2.84 GPa
412 ksi
DIN 53452; ASTM D790
Izod Impact, Notched 1.96 J/cm
3.67 ft-lb/in
DIN 53453; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
DIN 53752; ASTM D696
Melting Point 220 °C
428 °F
DIN 53736; ASTM D789
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
DIN 53461; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
DIN 53461; ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Constant 3.5

@Frequency 1e+6 Hz
3.5

@Frequency 1e+6 Hz
ASTM D150/DIN 53483
Dielectric Strength 22.0 kV/mm
559 kV/in
ASTM D149/DIN 53481
Arc Resistance 130 sec
130 sec
ASTM D495