Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler , Polypropylene, Mineral Reinforced
Manufacturer LG Chemical
Trade Name LUPOL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOL LW4302 PP+GF/MF30%.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PP+GF/MF30%, Low WarpageApplication: Electrical, Electronic and Automotive Parts CAS: 9003-07-0, 14807-96-6 and 165997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 68.6 MPa

@Thickness 3.20 mm
 9960 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break >= 10 %

@Thickness 3.20 mm
 >= 10 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 98.1 MPa

@Thickness 6.40 mm
 14200 psi

@Thickness 0.252 in
 1.3mm/min; ASTM D790
Flexural Modulus 5.49 GPa

@Thickness 6.40 mm
 797 ksi

@Thickness 0.252 in
 1.3mm/min; ASTM D790
Izod Impact, Notched >= 1.18 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 >= 2.20 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 150 °C

@Thickness 3.20 mm
 302 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness >=1.50 mm
 149 °F

@Thickness >=0.0591 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness >=1.50 mm
 149 °F

@Thickness >=0.0591 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness >=1.50 mm
 149 °F

@Thickness >=0.0591 in
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
Processing Properties Metric English Comments
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Middle Barrel Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Front Barrel Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Nozzle Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm