- Samyang Trirex® 3025GN10 Polycarbonate, Reinforced Flame Retardancy
Samyang Trirex® 3025GN10 Polycarbonate, Reinforced Flame Retardancy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3025GN10 Polycarbonate, Reinforced Flame Retardancy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3025GN10 is a reinforced flame retardant grade.Applications: LCD Panel Frame (dimensional stability)Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.13 % | 0.13 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength | 78.5 MPa | 11400 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 98.1 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 3.14 GPa | 455 ksi | ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.17 mm |
0.735 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.0 µm/m-°C | 23.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.97 | 2.97 | ASTM D150 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | ASTM D149 |
| Dissipation Factor | 0.0096 | 0.0096 | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Osprey Metals Fe30Cr Binary Alloy Powder (Grade 95% - 16)
- Eastman Eastar GN101 PETG Copolyester (discontinued **)
- Polimeri Europa Koblend P 475E Polystyrene-Polyolefin Alloy (discontinued **)
- LG Chemical LI921NS ASA
- Dow Nordel® IP 4640 Molded Brake Cup
- Eurotec® Tecotek® PC40 GR30 NL PC, 30% glass fiber reinforced, natural
- Aclo Accutech Polypropylene Homopolymer HP0334W40L1 Wollastonite Reinforced
- BLUESTAR LXS 112 PPE-PS
- PlastxWorld CEVIAN® S5220 20% GF PC/ABS alloy
Copyright © lookpolymers.com All Rights Reserved