Samyang Trirex® 3025GRU30 Polycarbonate, 30% Glass Reinforced

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled
Manufacturer	Samyang
Trade Name	Trirex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Samyang Trirex® 3025GRU30 Polycarbonate, 30% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries.Characteristics:30% milled glass fiberApplications:Particularly suitable for camera parts.All information provided by Samyang

Physical Properties	Metric	English	Comments
Specific Gravity	1.34 g/cc	1.34 g/cc	ASTM D792
Water Absorption	0.12 % @Time 86400 sec	0.12 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage	0.0030 - 0.0050 cm/cm @Thickness 3.00 mm	0.0030 - 0.0050 in/in @Thickness 0.118 in	ASTM D955
Melt Flow	25 g/10 min @Load 1.20 kg, Temperature 300 °C	25 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	122	122	ASTM D785
Tensile Strength, Yield	78.5 MPa	11400 psi	ASTM D638
Elongation at Break	9.0 %	9.0 %	ASTM D638
Flexural Yield Strength	98.1 MPa	14200 psi	ASTM D790
Flexural Modulus	3.33 GPa	484 ksi	ASTM D790
Izod Impact, Unnotched	0.981 J/cm @Thickness 3.17 mm	1.84 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	19.0 µm/m-°C	10.6 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	150 °C	302 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	144 °C	291 °F	ASTM D648
Flammability, UL94	HB @Thickness 1.59 mm	HB @Thickness 0.0625 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.00e+16 ohm-cm	4.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.29 @Frequency 1.00e+6 Hz	3.29 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	31.0 kV/mm	787 kV/in	ASTM D149
Dissipation Factor	0.0097 @Frequency 1.00e+6 Hz	0.0097 @Frequency 1.00e+6 Hz	ASTM D150
Arc Resistance	120 sec	120 sec	ASTM D495

Processing Properties	Metric	English
Rear Barrel Temperature	280 - 300 °C	536 - 572 °F
Middle Barrel Temperature	280 - 300 °C	536 - 572 °F
Front Barrel Temperature	280 - 300 °C	536 - 572 °F
Nozzle Temperature	290 - 310 °C	554 - 590 °F
Melt Temperature	300 - 310 °C	572 - 590 °F
Drying Temperature	120 °C	248 °F
Dry Time	3 - 5 hour	3 - 5 hour
Moisture Content	<= 0.020 %	<= 0.020 %
Screw Speed	30 - 80 rpm	30 - 80 rpm