LG Chemical LUCON CP6052 PC/ABS+CNT
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON CP6052 PC/ABS+CNT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description Injection Molding Grade, PC/ABS+CNT, Electrostatic Dissipation, Low Surface Resistivity, Improved Impact StrengthApplication: Laser diode Tray, ATM parts, Telecommunication Station Housing,CAS No. 103598-77-2, 9003-56-9, 181028-79-5 and 1333-86-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.7 MPa @Thickness 3.20 mm |
9250 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | >= 10 % @Thickness 3.20 mm |
>= 10 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa @Thickness 6.40 mm |
14200 psi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 2.94 GPa @Thickness 6.40 mm |
427 ksi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.441 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.827 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C @Thickness 6.40 mm |
243 °F @Thickness 0.252 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+7 ohm | 10000 - 1.00e+7 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 300 °C | 500 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 270 - 310 °C | 518 - 590 °F | Injection Molding |
| Front Barrel Temperature | 270 - 310 °C | 518 - 590 °F | Injection Molding |
| Nozzle Temperature | 270 - 310 °C | 518 - 590 °F | Injection Molding |
| Melt Temperature | 270 - 310 °C | 518 - 590 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 5.00 - 7.00 hour | 5.00 - 7.00 hour | Injection Molding |
| Back Pressure | 0.000 - 1.96 MPa | 0.000 - 284 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Huntsman Araldite GZ 7488 V-40 Bisphenol A Epoxy Solution
- Huntsman HY 265 Cycloaliphatic Amine
- Magyar Aluminum ALOLT 60F Aluminum Hydroxide
- Wieland Porta PressOver PFM Alloy
- Covestro Desmopan® 786 Thermoplastic Polyurethane
- Elastocon TPE Technologies Elastocon® CLR75 Thermoplastic Elastomer
- Arkema Group Rilsan® BECN TL Nylon 11, Sheathing Grade (Conditioned)
- BASF 4,7,10-Trioxatridecane-1,13-Diamine
- 3M Scotchcal™ 8000-25 Graphic Film
- Sax Polymers SAXALEN PPH329B20 Polypropylene Homopolymer, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved