Polymer Property : Flexural Strength = 170 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	170 MPa	24700 psi
Plastcom SLOVAMID 66 GF 10 PA66, 10% glass fibre Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0..
Flexural Strength	170 MPa	24700 psi	STN EN ISO 178
Plastcom SLOVASTER® B GF 20 Polybutylene Terephthalate, 20% Glass Fiber FeaturesPBT for injection moulding, chemically reinforced with 20% glass fiber. Characterized by excellent properties also at low temperatures like tensile and flexural modulus, tensile strength, a..
Flexural Strength	170 MPa	24700 psi	ISO 178
Nilit FRIANYL A63 GV15 Nylon 6.6 for injection molding, 15% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	170 MPa	24700 psi	Result based on similar products; ISO 178
Victrex® PEEK 150UF10 Polyetheretherketone Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, fine powder for composite manufacture, easy flow, FDA food contact compliant..
Flexural Strength	170 MPa	24700 psi	ASTM D790
LG Chemical LUMAX HR-5306F Heat Resistant PBT, 30% Polymer Alloy, Weather Resistant, Flame Retardant LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r..
Flexural Strength	170 MPa	24700 psi	ASTM D790
Mitsui Arlenâ„¢ A315 15% Glass Fiber-Reinforced Modified Nylon 6T (COND) ARLENâ„¢ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320Â°C) and a rigidity level comparable to super engineering plastics, it poss..
Flexural Strength	170 MPa @Strain 3.80 %	24700 psi @Strain 3.80 %	2 mm/min; ISO 178-A
Lanxess PocanÂ® ECO T 3215 000000 PBT + PET, 15% Glass Fiber PBT + PET, 15% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS.
Flexural Strength	170 MPa	24700 psi	2 mm/min; ISO 178
Lavergne VYPET VNT 340 PET 40% Glass - Mineral Reinforced Vypet VNT 340 is a 40% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications, with High Dielectric StrengthFeatures: High temperature performanc..
Flexural Strength	170 MPa @Strain 3.20 %	24700 psi @Strain 3.20 %	2 mm/min; ISO 178-A
Lanxess PocanÂ® TP 740-202 901510 PBT+ASA, 20% Glass Fiber PBT + ASA, 20% glass fibers, injection molding, low tendency to warp, improved surface finishInformation provided by LANXESS.
Flexural Strength	170 MPa @Strain 3.50 %, Temperature 100 Â°C	24700 psi @Strain 3.50 %, Temperature 212 Â°F	4; ISO 178
Solvay Specialty Polymers AmodelÂ® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Dry) AmodelÂ® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high stre..
Flexural Strength	170 MPa	24700 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DE002ER PC (Asia Pacific) LNP STAT-KON* DE002ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Flexural Strength	170 MPa	24700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 412 PBT (Europe-Africa-Middle East) VALOX 412 is 20% glass reinforced PBT injection moulding resin. Applications: Spotlights, appliance housings and handles.
Flexural Strength	170 MPa	24700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP OF006 PPS - Linear LNP* THERMOCOMP* OF006 is a compound based on Linear PPS containing 30% Glass Fiber.
Flexural Strength	170 MPa	24700 psi	ISO 178
Unitika BV2120G30 PA66, 30% Glass Fiber Reinforced, Flame Retardant, Conditioned Information provided by Unitika Ltd.
Flexural Strength	170 MPa	24700 psi	ASTM D790
Polyram PlusTek PA865G6 Nylon 6.6, 30% Glass Fiber 30% glass fiber reinforced, impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	170 MPa	24700 psi	ASTM D790
Polyram PlusTek PB320G6 Nylon 6, 30% Glass Fiber, Flame Retardant 30% glass-fiber reinforced, flame retardant polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	170 MPa	24700 psi	ISO 178-93
Wellman Wellamid® MRGF25/15 42H-BK167A Nylon 6, 25% Mineral and 15% Glass Fiber Reinforced GM 167A Black color matchAll information provided by Wellman Engineered Resins.
Flexural Strength	170 MPa @Thickness >=1.50 mm	24700 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola Etronit AS Phenolic, Paper Reinforcement, Black, Sheets Description: ESD-protection quality according to SP-method 2472, IEC 61340-5-1 and EN 100015-1. SP ESD Approval Certificate No. 230-01-0137. High mechanical properties at temperatures up to 120°CAp..
Flexural Strength	170 MPa @Thickness >=1.50 mm	24700 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola Etronit IIQ S Phenolic, Paper Reinforcement, Black, Sheets Description: Mechanically a good Etronit type with electrical properties adequate for insulation in low-voltage applications. Material is black throughout. Elegant surface finish combined with good ..
Flexural Strength	170 MPa	24700 psi	ISO 178
DuPont Performance Polymers Crastin® SK643FR NC010 Polybutylene Terephthalate (PBT) 20% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin SK643FR is a flame retardant 20% glass reinforced polybutylene terephthalate molding resin. It is recognized as UL94V-0 at 0.8..
Flexural Strength	170 MPa	24700 psi	ISO 178
Eurotec® Tecomid® NB40 KK30 NL PA 6 30% glass fiber/mineral reinforced, low warpage Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
Flexural Strength	170 MPa @Temperature 65.0 °C	24700 psi @Temperature 149 °F	ASTM Test
BASF Petra® 130 30% Glass Filled PET Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate (PET) for injection molding applications. It exhibits a good combination of performance properties including high strength and s..
Flexural Strength	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	ASTM Test
BASF Ultramid® 8202 PA6 (Dry) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult..
Flexural Strength	170 MPa	24700 psi	ASTM D790
BLUESTAR 201G20 PBT, 20% Glass Filled Typical Applications: Energy saving lightingInformation provided by Polymer Technology and Services, LLC (PTS).
Flexural Strength	170 - 193 MPa	24700 - 28000 psi
Bulk Molding Compounds BMC T60-6002-WG(15) Wear Resistant Molding Compound BMC T60-6002-WG-(15) is a wear resistant molding compound specifically formulated for applications that require excellent abrasion resistance. Due to its low specific gravity it has substantial cos..
Flexural Strength	170 MPa	24700 psi	ASTM D790
A. Schulman ComAlloy Comtuf® 463 Glass Reinforced, Impact Modified, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
Flexural Strength	170 MPa	24700 psi	ISO 178
Borealis Xmod™ GB306SAF Polypropylene, Glass Fiber Reinforced Xmod™ GB306SAF is a 35 % chemically coupled high performance glass fiber reinforced polypropylene compound intended for injection molding. The product is available in standard black 9502. This mat..
Flexural Strength	170 MPa @Temperature 100 °C	24700 psi @Temperature 212 °F	3.5% Strain; ISO 178
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA) (Unverified Data**) Amodel A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength..