SABIC Innovative Plastics LNP THERMOCOMP DF0081PI PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF0081PI PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF0081PI is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High Modulus, good flatness, Non-Brominated & Non-Chlorinated Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0041 cm/cm | 0.0041 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 123 MPa | 17800 psi | 5 mm/min; ISO 527 |
| 130 MPa | 18900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| 1.9 % | 1.9 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 12.5 GPa | 1810 ksi | 1 mm/min; ISO 527 |
| 12.7 GPa | 1840 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 170 MPa | 24700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.8 GPa | 1570 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.810 J/cm | 1.52 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.64 J/cm | 4.95 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- NYCOA 2012 Copolymer Nylon
- Parker Chomerics CHO-SHIELD® 576 Part A Conductive Coating
- Petroquimica Triunfo Trithene® TX 7001 LDPE - High Molecular Weight
- Multibase Multi-Flex® TEA 1004 TPO Thermoplastic Polyolefin Elastomer
- Meehanite GE-30 Flake Graphite Cast Iron
- SABIC Innovative Plastics ULTEM 1010R PEI (Asia Pacific)
- SSAB Tunnplat Dogal B420 Metal-coated Mild Steel
- Shinkong Synthetic Fibers Shinite® T102 PET, Fire Retardant
- Ametek Tungsten-Copper Composites AWC 8812
- Beijing Evergrow Resources ACFC1750 Activated Carbon Fiber Cloth
Copyright © lookpolymers.com All Rights Reserved