Lanxess Pocan® DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PET + PBT, 44% glass fibers/mineral, injection molding, LDS, high thermal dimensional stabilityInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | ISO 1183 |
| Bulk Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 60 |
| Viscosity Test | 50 cm³/g | 50 cm³/g | Viscosity number; ISO 1628-5 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 280°C / WZ 110°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0070 cm/cm | 0.0070 in/in | 60x60x2; 280°C / WZ 110°C; 600 bar; ISO 294-4 | |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 280 °C |
21 g/10 min @Load 4.76 lb, Temperature 536 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 12.7 GPa | 1840 ksi | ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 170 MPa @Strain 1.70 % |
24700 psi @Strain 1.70 % |
2 mm/min; ISO 178-A |
| Flexural Modulus | 12.8 GPa | 1860 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ISO 8302 |
| Melting Point | 255 °C | 491 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1, -2 |
| Vicat Softening Point | 225 °C @Load 5.10 kg |
437 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+20 ohm-cm | 2.00e+20 ohm-cm | IEC 60093 |
| Surface Resistance | 5.40e+16 ohm | 5.40e+16 ohm | IEC 60093 |
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.3 @Frequency 100 Hz |
4.3 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm @Thickness 1.00 mm |
838 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.0022 @Frequency 100 Hz |
0.0022 @Frequency 100 Hz |
IEC 60250 |
| 0.0138 @Frequency 1.00e+6 Hz |
0.0138 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 275 V | 275 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 110 °C | 230 °F | for test specimens; ISO 294 |
| 100 - 130 °C | 212 - 266 °F | ||
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 - 8 hour | 4 - 8 hour | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 7792-1-PET+PBT, GHMR, 07-120, (GF+MD)44 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 350ºF Cure Temperature
- LyondellBasell Petrothene® NA271009 Medium Density Polyethylene
- Menzolit Menzolit® BMC 2500 Unsaturated Polyester UP
- Grupo Repol Dinalon® B1S25 H PA6 Heat Stabilized
- Gwent Electronic Materials C2041206P2 Gold Polymer Electrode Paste
- Sibur DSSK-2545-M27 Oil-Filled Styrene-Butadiene Rubber
- Cheng Yu Plastic SW02 POM/PTFE
- Dow Corning SYL-OFF® 7040 COATING
- Elmer's Products Aron Alpha® 202 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- Ashley Polymers Ashlene® 73M Nylon 6, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved