Polykemi AB SCANMID 6 B32^ EF F15 Nylon 6, Glass Fiber Reinforced, Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled , Nylon 6, 20% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name SCANMID 6
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Polykemi AB SCANMID 6 B32^ EF F15 Nylon 6, Glass Fiber Reinforced, Modified.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Filler Content 15 %
15 %
±2%; Polykemi
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
With Flow; ISO 2577
0.0090 cm/cm
0.0090 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 75
<br>@Time 15.0 sec
 75
<br>@Time 0.00417 hour
 ASTM D2240
Tensile Strength at Break <= 120 MPa
<= 17400 psi
ISO/R527
Elongation at Break 6.0 %
6.0 %
ISO/R527
Flexural Strength <= 170 MPa
<= 24700 psi
ISO 178
Flexural Modulus 4.50 GPa
<br>@Temperature 23.0 °C
 653 ksi
<br>@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 1.00 J/cm²
<br>@Temperature -20.0 °C
 4.76 ft-lb/in²
<br>@Temperature -4.00 °F
 ISO 179
1.60 J/cm²
<br>@Temperature 23.0 °C
 7.61 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
120°C/h; ISO 75/1
Vicat Softening Point >= 200 °C
<br>@Load 5.001 kg
 >= 392 °F
<br>@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB
<br>@Thickness 1.60 mm
 HB
<br>@Thickness 0.0630 in
Glow Wire Test 650 °C
<br>@Thickness 2.00 mm
 1200 °F
<br>@Thickness 0.0787 in
 IEC 695-2-1