Lehmann & Voss LUVOCOM® 1700-7859 PPO, with carbon fiber, glass fiber and PTFE
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1700-7859 PPO, with carbon fiber, glass fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Improved friction and wear behaviour. Emergency running property.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Water Absorption | <= 0.060 % | <= 0.060 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 115 MPa | 16700 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 170 MPa | 24700 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 °C | 536 °F | mass temp |
| Nozzle Temperature | 285 - 295 °C | 545 - 563 °F | |
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |
| Zone 2 | 270 - 300 °C | 518 - 572 °F | |
| Zone 3 | 290 - 305 °C | 554 - 581 °F | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | |
| Drying Temperature | 95.0 - 110 °C @Time <=7200 sec |
203 - 230 °F @Time <=2.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A12^ Nylon 66
- Mitsui AURUM® JCL3030 Polyimide, Carbon Fiber Filled (discontinued **)
- Huntsman AroCy XU 378 Cyanate Ester
- GRECO ISOTHANE 1055D Poly(adipate)ester TPUÂ Resin
- SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP UCF26AS PPA
- ExxonMobil Exxsol™ D220/240 Dearomatized Fluid
- DuPont Performance Polymers Zytel® RS 3261TL NC010 Nylon 610 (Unverified Data**)
- 3M 5126 (Clear) Polyethylene Protective Tapes
- 3M Scotch-Weld™ 1300L Neoprene High Performance Rubber Gasket Adhesives
Copyright © lookpolymers.com All Rights Reserved