Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties.Features: Good Chemical Resistance; Good Creep Resistance; Good Flow; Good Stiffness; Heat Stabilized; High Heat Resistance; High Stiffness; High Strength; Hot Water Moldability; Low Moisture AbsorptionUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Connectors; Electrical Housing; Electrical/Electronic Applications; General Purpose; Housings; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Power/Other Tools; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D6779 PA101G35; GM GMP.PPA.021 Color: Black; GM GMP.PPA.021 Color: Natural; GM GMW16362P-PPA-GF35 Color: BlackInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Filler Content | 35 % | 35 % | Glass Fiber |
| Water Absorption | 0.29 % @Time 86400 sec |
0.29 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
| 0.0060 cm/cm | 0.0060 in/in | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength at Break | 82.0 MPa @Temperature 175 °C |
11900 psi @Temperature 347 °F |
4; ISO 527-2 |
| 92.4 MPa @Temperature 150 °C |
13400 psi @Temperature 302 °F |
4; ISO 527-2 | |
| 121 MPa @Temperature 100 °C |
17500 psi @Temperature 212 °F |
4; ISO 527-2 | |
| 211 MPa @Temperature 23.0 °C |
30600 psi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Tensile Strength | 203 MPa | 29400 psi | ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| 2.0 % @Temperature 23.0 °C |
2.0 % @Temperature 73.4 °F |
ISO 527-2 | |
| 4.3 % @Temperature 100 °C |
4.3 % @Temperature 212 °F |
ISO 527-2 | |
| 4.7 % @Temperature 175 °C |
4.7 % @Temperature 347 °F |
ISO 527-2 | |
| 4.9 % @Temperature 150 °C |
4.9 % @Temperature 302 °F |
ISO 527-2 | |
| Tensile Modulus | 13.8 GPa | 2000 ksi | ASTM D638 |
| 5.31 GPa @Temperature 175 °C |
770 ksi @Temperature 347 °F |
4; ISO 527-2 | |
| 6.27 GPa @Temperature 150 °C |
909 ksi @Temperature 302 °F |
4; ISO 527-2 | |
| 7.31 GPa @Temperature 100 °C |
1060 ksi @Temperature 212 °F |
4; ISO 527-2 | |
| 11.5 GPa @Temperature 23.0 °C |
1670 ksi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Flexural Strength | 310 MPa | 45000 psi | ASTM D790 |
| 112 MPa @Strain 3.50 %, Temperature 175 °C |
16200 psi @Strain 3.50 %, Temperature 347 °F |
4; ISO 178 | |
| 123 MPa @Strain 3.50 %, Temperature 150 °C |
17800 psi @Strain 3.50 %, Temperature 302 °F |
4; ISO 178 | |
| 170 MPa @Strain 3.50 %, Temperature 100 °C |
24700 psi @Strain 3.50 %, Temperature 212 °F |
4; ISO 178 | |
| 300 MPa @Strain 3.50 %, Temperature 23.0 °C |
43500 psi @Strain 3.50 %, Temperature 73.4 °F |
4; ISO 178 | |
| Flexural Modulus | 11.4 GPa | 1650 ksi | ASTM D790 |
| 4.60 GPa @Temperature 175 °C |
667 ksi @Temperature 347 °F |
ISO 178 | |
| 4.90 GPa @Temperature 150 °C |
711 ksi @Temperature 302 °F |
ISO 178 | |
| 6.60 GPa @Temperature 100 °C |
957 ksi @Temperature 212 °F |
ISO 178 | |
| 11.4 GPa @Temperature 23.0 °C |
1650 ksi @Temperature 73.4 °F |
ISO 178 | |
| Compressive Strength | 148 MPa | 21500 psi | ASTM D695 |
| Poissons Ratio | 0.39 | 0.39 | ASTM E132 |
| Shear Strength | 87.6 MPa | 12700 psi | ASTM D732 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.10 kJ/m² | 4.33 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 0.920 J/cm² | 4.38 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature 100 - 200 °C |
8.89 µin/in-°F @Temperature 212 - 392 °F |
2 |
| 22.0 µm/m-°C @Temperature 0.000 - 100 °C |
12.2 µin/in-°F @Temperature 32.0 - 212 °F |
2 | |
| CTE, linear, Transverse to Flow | 61.0 µm/m-°C @Temperature 0.000 - 100 °C |
33.9 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 100 µm/m-°C @Temperature 100 - 200 °C |
55.6 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 310 °C | 590 °F | ISO 11357-3 |
| 310 °C | 590 °F | DSC | |
| Deflection Temperature at 0.46 MPa (66 psi) | 303 °C | 577 °F | HDT B; Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 288 °C | 550 °F | Unannealed; ISO 75-2/A |
| 291 °C @Thickness 3.20 mm |
556 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 316 - 321 °C | 601 - 610 °F | |
| Front Barrel Temperature | 327 - 332 °C | 621 - 630 °F | |
| Melt Temperature | 321 - 335 °C | 610 - 635 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.045 % | <= 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Processing Technique | Water-Heated Mold Injection Molding |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR MBT
- Lucent Polymers PC/ABS-1216LG Polycarbonate+ABS, Low Gloss, Injection Grade
- Karina E 36/597-FC-LMP MB Concentration of Pigment Brown for PVC
- Techmer ES HiFill® PA6 E U
- Techmer ES Plastiblend® PPS 05003
- A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- ChevronTexaco ISO 150 Ultra Gear Lubricant
- ExxonMobil 22 Mobil EAL Arctic Series
- ACC QSil 60 QSI Quantum Silicones 50 Durometer Condensation Cure for Potting