Manifattura Cattaneo PEEK Polyetheretherketone
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PEEK Polyetheretherketone.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 - 1.32 g/cc | 0.0455 - 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
50% RH; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 99 | 99 | ASTM D785 |
| Tensile Strength at Break | 94.0 MPa | 13600 psi | ASTM D638 |
| Tensile Strength, Yield | 88.0 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 20 - 60 % | 20 - 60 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | ASTM D790 |
| Compressive Strength | 122 MPa | 17700 psi | ASTM D695 |
| Poissons Ratio | 0.40 | 0.40 | |
| Izod Impact, Notched (ISO) | 6.10 kJ/m² | 2.90 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | NB | NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.22 | 0.22 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 3.9 | 3.9 | µm/s. PV = 0.1 MPa-m/s; max P = 30 MPa; MPC Test |
| Limiting Pressure Velocity | 1.90 MPa-m/sec | 54200 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature 23.0 - 100 °C |
26.1 µin/in-°F @Temperature 73.4 - 212 °F |
|
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM D177 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648-45 |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 24 - 35 % | 24 - 35 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dielectric Loss Index | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| UV Resistance | Y |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SHIELD® 4076 Conductive Coating
- Polymer Resources NY6-G43-[color]-H Nylon 6, 43% Glass Reinforced, Heat Stabilized
- Manifattura Cattaneo RULON® 641 Polytetrafluoroethylene
- A. Schulman POLYBATCH™ CE-505-B Concentrate Based In Polyethylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.5 PHR Sulfur
- Epoxy Technology EPO-TEK® E3001-6 Electrically Conductive, Silver Epoxy
- ExxonMobil Vistalon™ 878P Ethylene Propylene Copolymer Rubber
- BASF Palatinol® TOTM Tri Octyl Trimellitate
Copyright © lookpolymers.com All Rights Reserved