BASF Ultramid® 8202 HS PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8202 HS PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.

Physical Properties	Metric	English	Comments
Density	0.932 g/cc	0.0337 lb/in³	Melt; ISO 1183
	1.13 g/cc	0.0408 lb/in³	ISO 1183
Water Absorption	1.6 %	1.6 %	24 hour; ISO Test
	9.5 %	9.5 %	ISO 62
Moisture Absorption at Equilibrium	2.7 %	2.7 %	23°C/50% R.H.; ISO 62
Relative Viscosity	2.6 cP	2.6 cP	ISO Test; 96 % SAV
Viscosity Measurement	48	48	Formic Acid
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	119	119	ASTM Test
Tensile Strength at Break	75.0 MPa	10900 psi	0.2 in/min; ASTM Test
Tensile Strength, Yield	78.0 MPa	11300 psi	50mm/min; ISO 527
	79.0 MPa	11500 psi	2 in/min; ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO Data
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM Test
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ASTM Test
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ISO Data
	126 MPa @Temperature -40.0 °C	18300 psi @Temperature -40.0 °F	ASTM Test
	126 MPa @Temperature -40.0 °C	18300 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	25 %	25 %	50mm/min, Nominal strain; ISO 527
	55 %	55 %	2 in/min; ASTM Test
Elongation at Yield	4.0 %	4.0 %	50mm/min; ISO 527
	4.0 %	4.0 %	2 in/min; ASTM Test
	36 % @Temperature 120 °C	36 % @Temperature 248 °F	ISO Data
	36 % @Temperature 120 °C	36 % @Temperature 248 °F	ASTM Test
	42 % @Temperature 80.0 °C	42 % @Temperature 176 °F	ISO Data
	42 % @Temperature 80.0 °C	42 % @Temperature 176 °F	ASTM Test
Tensile Modulus	2.70 GPa	392 ksi	1mm/min; ISO 527
	0.360 GPa @Temperature 120 °C	52.2 ksi @Temperature 248 °F	ISO Data
	0.485 GPa @Temperature 80.0 °C	70.3 ksi @Temperature 176 °F	ISO Data
Flexural Strength	85.0 MPa	12300 psi	ISO Data
	108 MPa	15700 psi	ASTM Test
	17.0 MPa @Temperature 120 °C	2470 psi @Temperature 248 °F	ASTM Test
	20.0 MPa @Temperature 93.0 °C	2900 psi @Temperature 199 °F	ASTM Test
	30.0 MPa @Temperature 65.0 °C	4350 psi @Temperature 149 °F	ASTM Test
	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	2.40 GPa	348 ksi	ISO Data
	2.83 GPa	410 ksi	ASTM Test
	0.305 GPa @Temperature 120 °C	44.2 ksi @Temperature 248 °F	ASTM Test
	0.350 GPa @Temperature 93.0 °C	50.8 ksi @Temperature 199 °F	ASTM Test
	0.500 GPa @Temperature 65.0 °C	72.5 ksi @Temperature 149 °F	ASTM Test
Izod Impact, Notched	0.480 J/cm @Temperature -40.0 °C	0.899 ft-lb/in @Temperature -40.0 °F	ASTM Test
	0.580 J/cm @Thickness 3.17 mm	1.09 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact Unnotched	NB	NB	ISO 179
	5.10 J/cm² @Temperature -30.0 °C	24.3 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.350 J/cm²	1.67 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	83.0 µm/m-°C @Temperature -30.0 - 30.0 °C	46.1 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Specific Heat Capacity	3.728 J/g-°C	0.8910 BTU/lb-°F	Melt
Thermal Conductivity	0.264 W/m-K	1.83 BTU-in/hr-ft²-°F	Melt
Melting Point	220 °C	428 °F	10 K/min
Deflection Temperature at 0.46 MPa (66 psi)	150 °C	302 °F	ISO 75
	178 °C	352 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	ISO 75
	65.0 °C	149 °F	ASTM Test
Flammability, UL94	V-2 @Thickness 0.700 mm	V-2 @Thickness 0.0276 in
	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	4.1 @Frequency 1.00e+6 Hz	4.1 @Frequency 1.00e+6 Hz	ASTM Data
	4.3 @Frequency 1e+9 Hz	4.3 @Frequency 1e+9 Hz	ASTM Data
Dielectric Strength	37.0 kV/mm	940 kV/in	IEC 60243-1
Dissipation Factor	0.010 @Frequency 1e+9 Hz	0.010 @Frequency 1e+9 Hz	ASTM Data
	0.010 @Frequency 1.00e+6 Hz	0.010 @Frequency 1.00e+6 Hz	ASTM Data
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	260 °C	500 °F	Injection molding
Mold Temperature	80.0 °C	176 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes