Polyram RamTal PM3009G4 Polyacetal for Injection Molding, 20% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 20% Glass Fiber Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM3009G4 Polyacetal for Injection Molding, 20% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber reinforced polyacetal for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.010 cm/cm | 0.0040 - 0.010 in/in | ISO 2577 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 180 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 356 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- MV Labs IN500 InF3 Indium(III) fluoride
- Resin Technology Group 1105 Oxy-Bond™ Two-Component Epoxy Adhesive
- SABIC Innovative Plastics Lexan® HP6 PC
- Indium Corp. Indalloy® 42 Bi-Sn-Pb Solder Alloy
- Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched
- Diamond Polymers NPP25-1503 GF10 Glass Filled Copolymer Polypropylene
- Fainplast Compounds GS 69/P Flexible PVC, Injection Molding for Footwear
- Fainplast Compounds CKL 80/3 Flexible PVC, Sheathing Lead Free
- 3M FV092 Soft Translucent Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved