Polyram PlusTek PA865G6 Nylon 6.6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA865G6 Nylon 6.6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | DIN 53479 |
| Water Absorption | 4.5 % | 4.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM-D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM-D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM-D638 |
| Flexural Strength | 170 MPa | 24700 psi | ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM-D790 |
| Izod Impact, Notched | 2.50 J/cm @Temperature 23.0 °C |
4.68 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| >= 200 °C | >= 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2205-25 CR-SX Fiberglass Reinforced SMC
- SABIC Innovative Plastics LNP THERMOCOMP MX85738 PP (Asia Pacific)
- ELASTO UK Dryflex® 400501S SBS Based Material, 50A Hardness, Natural
- Denka VINYKON M558070 PVC, M grade for soft injection molding
- Chosun Refractories APC-100G Acid-proof Castable
- DuPont Teijin Films Melinex® 329 Polyester Film, 700 Gauge
- Arkema Group OREVAC® 18732 Grafted Maleic Anhydride Polypropylene
- Arkema Group Orgalloy® RS 6635 A Polyamide 6.6 Alloy 35% Glass Fiber reinforced
- Braskem LL118 Blown Film Extrusion Linear Low Density Polyethylene
- Bulk Molding Compounds BMC 200 Thermoset Polyester, Electrical Grade
Copyright © lookpolymers.com All Rights Reserved