Unitika A3030N-2 PA6, 30% Mineral Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A3030N-2 PA6, 30% Mineral Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 3.20 mm |
0.0080 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527-1/-2 |
| Elongation at Break | 4.5 % | 4.5 % | ISO 527-1/-2 |
| Tensile Modulus | 5.40 GPa | 783 ksi | ISO 527-1/-2 |
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 0.850 mm |
V-2 @Thickness 0.0335 in |