Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | Unannealed; ASTM D648 |
PolyOne Gravi-Tech™ GT6000-0023 Black Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP Faradex ES003DE PEI LNP* Faradex* ES003DE is a Polyetherimide resin containing stainless steel fibers. Characteristics of this grade are EMI/RFI Shielding.This data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP FARADEX ES003E PEI LNP* FARADEX* ES003E is a Polyetherimide resin containing 15% Stainless Steel Fibers. Added feature of this grade is: EMI/RFI Shielding. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ASTM Data |
BASF Capron® SEG6 H1 30% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG6 H1 is a 30% glass reinforced nylon 6 injection molding compound. This material is currently under development as XA-2678. It exhibits exceptional surface aesthetics at the slower fill s.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | |
Covestro Apec® DP 1-9379 Polycarbonate
(discontinued **) Key Features:UnfilledSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and ha.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C @Thickness 3.20 mm |
381 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP STAT-KON PE002Z PA 6 LNP* STAT-KON* PE002Z is a compound based on Nylon 6 resin containing 10% Carbon Fiber. Added features of this grade include: Extrusion Grade. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C @Thickness 3.20 mm |
381 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 (Asia Pacific) LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP THERMOCOMP YF002 POLYESTER ELASTOMER LNP* THERMOCOMP* YF002 is a compound based on Poyester Elastomer containing 10% Glass Fiber. Added feature of this grade is: High Modulus. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C @Thickness 3.20 mm |
381 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ISO 75-1/-2 |
Unitika A3030N-2 PA6, 30% Mineral Reinforced, Dry Information provided by Unitika Ltd. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ISO 75-1/-2 |
Unitika RUN35-C25 PA6, Dry High modulus and low warpage nylonInformation provided by Unitika Ltd. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | |
Covestro Apec® HT KU 1-9373 High-Heat Polycarbonate Transparent and opaque shades possible, UV-stabilized.Applications: Lighting, automotive and household goods, light covers.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ASTM Data |
BASF Capron® SEG6 H1 BK-122 30% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG6 H1 BK-122 is a black pigmented, 30% glass reinforced nylon 6 injection molding compound. This material is currently under development as XA-2678. It exhibits exceptional surface aesthet.. |