Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 381 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F	Unannealed; ASTM D648
PolyOne Gravi-Tech™ GT6000-0023 Black Polyamide 6 (Nylon 6) Information provided by PolyOne
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Faradex ES003DE PEI LNP* Faradex* ES003DE is a Polyetherimide resin containing stainless steel fibers. Characteristics of this grade are EMI/RFI Shielding.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP FARADEX ES003E PEI LNP* FARADEX* ES003E is a Polyetherimide resin containing 15% Stainless Steel Fibers. Added feature of this grade is: EMI/RFI Shielding.
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F	ASTM Data
BASF Capron® SEG6 H1 30% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron SEG6 H1 is a 30% glass reinforced nylon 6 injection molding compound. This material is currently under development as XA-2678. It exhibits exceptional surface aesthetics at the slower fill s..
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F
Covestro Apec® DP 1-9379 Polycarbonate (discontinued **) Key Features:UnfilledSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and ha..
Deflection Temperature at 0.46 MPa (66 psi)	194 Â°C @Thickness 3.20 mm	381 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON PE002Z PA 6 LNP* STAT-KON* PE002Z is a compound based on Nylon 6 resin containing 10% Carbon Fiber. Added features of this grade include: Extrusion Grade.
Deflection Temperature at 0.46 MPa (66 psi)	194 Â°C @Thickness 3.20 mm	381 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 (Asia Pacific) LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 0.46 MPa (66 psi)	194 Â°C	381 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP THERMOCOMP YF002 POLYESTER ELASTOMER LNP* THERMOCOMP* YF002 is a compound based on Poyester Elastomer containing 10% Glass Fiber. Added feature of this grade is: High Modulus.
Deflection Temperature at 0.46 MPa (66 psi)	194 Â°C @Thickness 3.20 mm	381 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12 LNP* Thermocomp* IF002 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F	ISO 75-1/-2
Unitika A3030N-2 PA6, 30% Mineral Reinforced, Dry Information provided by Unitika Ltd.
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F	ISO 75-1/-2
Unitika RUN35-C25 PA6, Dry High modulus and low warpage nylonInformation provided by Unitika Ltd.
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F
Covestro Apec® HT KU 1-9373 High-Heat Polycarbonate Transparent and opaque shades possible, UV-stabilized.Applications: Lighting, automotive and household goods, light covers.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience..
Deflection Temperature at 0.46 MPa (66 psi)	194 °C	381 °F	ASTM Data
BASF Capron® SEG6 H1 BK-122 30% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron SEG6 H1 BK-122 is a black pigmented, 30% glass reinforced nylon 6 injection molding compound. This material is currently under development as XA-2678. It exhibits exceptional surface aesthet..