Total PPC 9712 Polypropylene, Heterophasic Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Total Atofina
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 9712 Polypropylene, Heterophasic Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ATOFINA Propylene 9712 is heterophasic copolymer. PPC 9712 is characterized by excellent impact resistance and antistatic properties and has been formulated to allow faster cycling through early demolding.

Physical Properties	Metric	English	Comments
Bulk Density	0.525 g/cc	0.0190 lb/in³	ISO 1183
Density	0.905 g/cc	0.0327 lb/in³	ISO 1183
Melt Flow	25 g/10 min @Load 2.16 kg, Temperature 230 °C	25 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	80	80	ISO 2039-2
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 527-2
Elongation at Yield	6.0 %	6.0 %	ISO 527-2
Tensile Modulus	1.15 GPa	167 ksi	ISO 527-2
Flexural Modulus	1.05 GPa	152 ksi	ISO 527-2
Izod Impact, Notched (ISO)	8.00 kJ/m²	3.81 ft-lb/in²	ISO 179
	5.50 kJ/m² @Temperature -20.0 °C	2.62 ft-lb/in² @Temperature -4.00 °F	ISO 179
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	Low Temp; ISO 179
	>= 4.00 J/cm²	>= 19.0 ft-lb/in²
	>= 4.00 J/cm²	>= 19.0 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C	194 °F	120°C per hour; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	48.0 °C	118 °F	120°C per hour; ISO 75-2
Vicat Softening Point	60.0 °C	140 °F	50N-50°C per hour; ISO 306
	130 °C	266 °F	10N-50°C per hour; ISO 306