Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 60.0 °C @Load 1.00 kg |
140 °F @Load 2.20 lb |
ISO 306/A |
Polimeri Europa Clearflex® MP D0 Very Low Density Polyethylene Clearflex MP D0 is a linear polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin shows an excellent balance between flexibility and impact resistance.Main Applicati.. |
|||
Vicat Softening Point | 60.0 °C @Load 1.00 kg |
140 °F @Load 2.20 lb |
ISO 306/A |
Polimeri Europa Greenflex® FF 55 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FF 55 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FF 55 show high flexibility.Main Applications: Greenflex FF 55 is recommended f.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | Rate B; ISO 306/B50 |
Premix Thermoplastics PRE-ELEC® PE 1294 PRE-ELEC PE 1294 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 129.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | |
Advanced Elastomer Systems Vistaflex® 671N Thermoplastic Rubber
(discontinued **) A translucent thermoplastic elastomer with snappiness. It can be processed using injection molding or extrusion processing techniques.Key Features: Flex modulus (1% Secant) 9.0 MPa (1300 psi); Vica.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
DuPont Bynel® E326 Acid-/Acrylate-Modified EVA Adhesive Resin
(discontinued **) Bynel® Series 3100 resins are acid/acrylate-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to proce.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | Rate B; ASTM D-1525 |
ExxonMobil Iotek® 7010 Zinc Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A zinc ionomer with excellent flexibility, abrasion resistance, impact strength and tensile strength. This ionomer has outstanding adhesion to glas.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | Rate B; ASTM D-1525 |
ExxonMobil Iotek® 7020 Zinc Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A zinc ionomer with excellent flexibility, abrasion resistance, impact strength and tensile strength. This ionomer has outstanding adhesion to glas.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | A; ISO 306 |
FKuR Kunststoff Bio-Flex® F 6510 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | VST/B/50; ISO 306 |
MBA Polymers PP 2126 Post-consumer recycled general purpose polypropylene impact copolymer Available in standard black.Information provided by MBA Polymers. |
|||
Vicat Softening Point | 60.0 °C @Load 5.00 kg |
140 °F @Load 11.0 lb |
|
LATI Latigea B01 F1 Bio-Polymer Bio-Polymer (PLA, PHB, ...). Unfilled. Potentially suitable for food/medical contact application. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pr.. |
|||
Vicat Softening Point | 60.0 °C @Load 5.00 kg |
140 °F @Load 11.0 lb |
|
LATI Latigray 47/1-01 CX/45 PP Copolymer Radiopaque compound based on Polypropylene copolymer (PPc). Special mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati .. |
|||
Vicat Softening Point | 60.0 °C @Load 5.00 kg |
140 °F @Load 11.0 lb |
|
LATI Latilub 37 B01-02S Bio-Polymer Self-lubricating product based on Bio-Polymer (PLA, PHB, ...). Silicone.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
DuPont Bynel® 3126 Adhesive Resin Bynel® Series 3100 resins are acid/acrylate-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to proce.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
DuPont Elvaloy® 3117 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3117 AC is intended for coextrusion and compounding. Due to its high melt flow rate, it is used also in extrusion coating. Elvaloy® 3117 AC is soft, flexible and has good adhesion to va.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
Westlake EMAC® SP2255 17% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2255 is a 17% EMA copolymer containing slip and antiblock. This resin is designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat s.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
DuPont Appeel® LSR20D751 Lidding Sealant Resin Appeel® LSR20D751 is a modified ethylene acrylate resin designed to function as a sealing layer for lidding applications. It is most often suggested to provide peelable seals over a broad temperatu.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
DuPont Bynel® 2002 Acid-Modified Ethylene Terpolymer Adhesive Resin Bynel® Series 2000 resins are acid-modified ethylene terpolymers with medium to high acid comonomer contents. They contain a temperature stable ester that makes them functional in high-temperature .. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
Chevron Phillips K-Resin® KR52 Styrene-Butadiene Copolymer Customer Benefits:Excellent Optical PropertiesGood StiffnessExcellent PrintabilityUp to 80% Shrinkage at 100°CBlends well with Polystyrene Typical Applications:Shrink Sleeve LabelsMulti-layer Films.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525, ISO 306 |
DuPont™ Surlyn® E185SB Ionomer Resin Surlyn® E185SB is an ionomer of an acid copolymer resin. It is designed for coextrusion with high-density polyethylene in peelable seals applications. It can be used in extrusion equipment designed.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
Arkema Group Orevac® 9318 Film EVA-MAH Terpolymer EVA Terpolymers based Main Applications: Extrusion coating Thermo-adhesive filmsInformation provided by Arkema Group |
|||
Vicat Softening Point | 60.0 °C | 140 °F | 50°C/hr; 50N |
Arkema Group Pebax® 2533 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 25 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | |
BASF Novolen® 3340 PC Polypropylene Nucleated grade for injection moldings with higher transparency.Data was collected by ISO methods and provided by BASF. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | |
BASF Procom® GC20S 400 Polypropylene Uses: electrical appliance housings (e.g. drills), components requiring high impact and temperature resistance, furniture frames.Data was collected by ISO methods and provided by BASF. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | 50°C/hr; 50N |
Arkema Group Appryl® 3130 MU 7 Polypropylene - Polyethylene Copolymer PP/PE copolymer colored during the injection molding process. This grade with a very good impact test at low temperature, has been developed for bumpers applications for the automotive industry. It .. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | B |
Plastcom SLOVALEN PQ 83 T 40 PP, 40% mineral filling FeaturesModified PP for injection moulding with the content of 40% mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased .. |
|||
Vicat Softening Point | 60.0 - 143 °C | 140 - 289 °F | Average value: 122 °C Grade Count:22 |
Overview of materials for Acetal Copolymer, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Impact Modified". Each property range of values reported is minimum and maximum values.. |
|||
Vicat Softening Point | 60.0 °C @Load 1.02 kg |
140 °F @Load 2.25 lb |
ASTM D1525 |
Arkema Group LOTRYL® 17 BA 04 Copolymer Ethylene - Butyl Acrylate LOTRYL® 17 BA 04 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. LOTRYL® 17 BA 04 is used as tie layer in coextrusion PP/PE, for extrusi.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | Rate B; ASTM D-1525 |
ExxonMobil Iotek® 7030 Zinc Ionomer Molding/Extrusion Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A zinc ionomer with excellent flexibility, abrasion resistance, impact strength and tensile strength. This ionomer has outstanding adhesion to glas.. |
|||
Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
DuPont Bynel® 2174 Anhydride-Modified Ethylene Acrylate Adhesive Resin
(discontinued **) Bynel® Series 2100 resins are anhydride-modified ethylene acrylate resins. They contain a temperature stable ester that makes them functional in high temperature coextrusions. They are available in.. |
|||
Vicat Softening Point | 60.0 - 156 °C | 140 - 313 °F | Average value: 133 °C Grade Count:58 |
Overview of materials for Polypropylene, Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Extrusion Grade". Each property range of values reported is minimum and maximum values of.. |