Styron EMERGEâ„¢ 7560 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	EMERGE™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron EMERGEâ„¢ 7560 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

EMERGEâ„¢ PC/ABS 7560 advanced resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. This resin is suitable for use in a wide variety of applications in the information technology equipment market.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.

Physical Properties	Metric	English	Comments
Bulk Density	0.665 g/cc	0.0240 lb/inÂ³	ISO 60
Density	1.17 g/cc	0.0423 lb/inÂ³	ISO 1183B
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0070 cm/cm	0.0070 in/in	ISO 294-4
Melt Flow	22 g/10 min @Load 3.80 kg, Temperature 230 Â°C	22 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ISO 1133
	100 g/10 min @Load 5.00 kg, Temperature 260 Â°C	100 g/10 min @Load 11.0 lb, Temperature 500 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ISO 2039/2
Tensile Strength at Break	45.0 MPa	6530 psi	50mm/min; ISO 527-2
Tensile Strength, Yield	60.0 MPa	8700 psi	50mm/min; ISO 527-2
Elongation at Break	50 %	50 %	50mm/min; ISO 527-2
Elongation at Yield	4.0 %	4.0 %	50mm/min; ISO 527-2
Tensile Modulus	2.55 GPa	370 ksi	1mm/min; ISO 527-2
Flexural Strength	98.0 MPa	14200 psi	2mm/min; ISO 178
Flexural Modulus	2.80 GPa	406 ksi	2mm/min; ISO 178
Izod Impact, Notched (ISO)	16.0 kJ/mÂ²	7.61 ft-lb/inÂ²	ISO 180/A
Charpy Impact, Notched	1.40 J/cmÂ²	6.66 ft-lb/inÂ²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Hot Ball Pressure Test	90.0 Â°C	194 Â°F	IEC 60335-1
Deflection Temperature at 0.46 MPa (66 psi)	94.0 Â°C	201 Â°F	unannealed; ISO 75-B
Deflection Temperature at 1.8 MPa (264 psi)	82.0 Â°C	180 Â°F	unannealed; ISO 75-A
Vicat Softening Point	100 Â°C	212 Â°F	50Â°C / 50N; ISO 306-B50
	108 Â°C	226 Â°F	120Â°C / 10N; ISO 306-A120
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	all colors
Oxygen Index	29 %	29 %	ISO 4589-2
Glow Wire Test	925 Â°C @Thickness 2.00 mm	1700 Â°F @Thickness 0.0787 in	(GWIT); IEC 60695-2-13
	960 Â°C @Thickness 2.00 mm	1760 Â°F @Thickness 0.0787 in	(GWFI); IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	>= 250 V @Thickness 3.00 mm	>= 250 V @Thickness 0.118 in	IEC 60112

Processing Properties	Metric	English
Melt Temperature	240 - 280 Â°C	464 - 536 Â°F
Mold Temperature	40.0 - 80.0 Â°C	104 - 176 Â°F
Drying Temperature	80.0 - 90.0 Â°C	176 - 194 Â°F
Dry Time	4 hour	4 hour