Total Lacqrene® 851 High Impact Polystyrene (discontinued **)

Category	Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Lacqrene® 851 High Impact Polystyrene (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LACQRENE® 851 is a flame retardant, high impact polystyrene, halogen free rated UL 94 V0 @ 2.5 mm and UL 94 5VA @ 2mm. LACQRENE® 851 offers rheological and mechanics properties which permits large moldings. ApplicationLACQRENE® 851(EU) is a flame retardant, high impact polystyrene, halogen free rated UL 94 V0 @ 2.5 mm and UL 94 5VA @ 2mm. LACQRENE® 851 offers rheological and mechanics properties which permits large moldings. Information provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Density	1.11 g/cc	0.0401 lb/in³	ISO 1183
Water Absorption	<= 0.10 %	<= 0.10 %	ISO 62
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in
Melt Flow	4.0 g/10 min @Load 5.00 kg, Temperature 200 °C	4.0 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133H
	12 g/10 min @Load 5.00 kg, Temperature 200 °C	12 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133H

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	40.0 MPa	5800 psi	ISO 527-2
Tensile Strength, Yield	40.0 MPa	5800 psi	ISO 572-2
Elongation at Break	40 %	40 %	ISO 527-2
Flexural Modulus	2.30 GPa	334 ksi	ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/m²	3.33 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	0.650 J/cm²	3.09 ft-lb/in²	ISO 1791/eU

Thermal Properties	Metric	English	Comments
Vicat Softening Point	92.0 °C	198 °F	50N (T° increase = 5°C/h); ISO 306B50
	100 °C	212 °F	10N (T° increase = 50°C/h); ISO 306A50

Processing Properties	Metric	English	Comments
Processing Temperature	<= 270 °C	<= 518 °F