- Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled
- Sumitomo Bakelite North America 52-70-70-VO-P Short-Glass Reinforced Diallyl Phthalate
Sumitomo Bakelite North America 52-70-70-VO-P Short-Glass Reinforced Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America 52-70-70-VO-P Short-Glass Reinforced Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Conforms with the requirements of ASTM D5948 Type SDG-F.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.91 g/cc | 0.0690 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | |
| Water Absorption | 0.25 % | 0.25 % | 48 hours, 50°C. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | Compression Molding. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Compressive Yield Strength | 150 MPa | 21800 psi | ASTM D695 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature 20.0 °C |
11.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL temperature Index, UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | ASTM D648A |
| UL RTI, Electrical | 130 °C | 266 °F | UL temperature Index, UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL temperature Index, UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL temperature Index, UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
Wet |
| Dielectric Strength | 13.8 kV/mm | 351 kV/in | Wet, step-by-step. ASTM D149 |
| Dissipation Factor | 0.014 @Frequency 1e+6 Hz |
0.014 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM D3638 (IEC 112) |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |