Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 160 - 235 °C | 320 - 455 °F | Average value: 221 °C Grade Count:9 |
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade". Each property range of values reported.. |
|||
Processing Temperature | 160 - 210 °C | 320 - 410 °F | |
Celanese Ateva® 1061 Ethylene Vinyl Acetate Copolymer Film
(discontinued **) Ateva® 1061 resin is suitable for laminating and co-extrusion applications with excellent sealability, opticals and strength. This EVA resin may be safely used as articles or components of article.. |
|||
Processing Temperature | 160 - 200 °C | 320 - 392 °F | |
Kraiburg TPE THERMOLAST® K TA6AAD Injection Molding TPE Compound easy printable, paintable, glueable without pretreatmentColorable in any shadeSubstitution for PVC and silicone rubberTypical Applications: ToysBaby productsPromotion articlesMaterial Advan.. |
|||
Processing Temperature | 160 - 200 °C | 320 - 392 °F | |
Kraiburg TPE THERMOLAST® K TA7AAA Technical TPE Compound easy printable, paintable, glueable without pretreatmentColorable in any shadeSubstitution for PVC and silicone rubberTypical Applications: ToysBaby productsPromotion articlesMaterial Advan.. |
|||
Processing Temperature | 160 - 190 °C | 320 - 374 °F | |
LG Chemical LUTENE BB0808 LDPE Blown Film Grade Description: LUTENE BB0808 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of shrink film and pallet shrink covers. LUTENE BB0808 have the balanc.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | |
Kraiburg TPE THERMOLAST® K TC9CCT Transparent Cable Extrusion TPE Transparent compound for cable extrusionSubstitute for PVC-P or siliconExtremely flexible materialFlexible in low temperaturesColoring in any shadeTypical Applications: Transmission cablesLoudspeake.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | |
Kraiburg TPE THERMOLAST® K TP5CCZ Black Cable Extrusion TPE Black compound for cable extrusionSubstitute for PVC-PExtremely flexible materialFlexible in low temperaturesOutdoor useTypical Applications: Transmission cablesLoudspeaker cablesConnecting cablesMa.. |
|||
Processing Temperature | 160 - 200 °C | 320 - 392 °F | |
Kraiburg TPE THERMOLAST® K TS4AAZ Black TPE Black compound for applications with reduced requirementsTypical Applications: GripsErasersGrips on stationeriesTransport protectionAnti-slip elementsSkirting boardMaterial Advantages: Excellent pri.. |
|||
Processing Temperature | 160 - 200 °C | 320 - 392 °F | |
Kraiburg TPE THERMOLAST® K TS5AAA Natural TPE Natural compound for applications with reduced requirementsTypical Applications: GripsErasersGrips on stationeriesTransport protectionAnti-slip elementsSkirting boardMaterial Advantages: Excellent p.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Membranes |
Lucobit Lucofin® 1411-t1 Polyolefin TPO Granules, White Lucofin are colored, highly stabilized polyolefin-based TPO granules. The t1 series is distinguished by good tenacity, high biaxial extensibility and flexibility outstanding breaking strength, and .. |
|||
Processing Temperature | 160 - 270 °C | 320 - 518 °F | Extrusion |
Lucobit Lucofin® 1494H Chemically Modified Polyethylene Lucofin® 1492 is a chemically modified polyethylene, i.e. EBA grafted with maleic anhydride (MA). Lucofin® 1492 can be used pure or as a component in mixtures applications where improved polar.. |
|||
Processing Temperature | 160 - 200 °C | 320 - 392 °F | Profiles and hoses |
Lucobit Lucofin® 1400SL Ethylene Butyl Acrylate Lucofin® 1400SL is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin® 1400SL is softer and more flexible than ethylene h.. |
|||
Processing Temperature | 160 - 230 °C | 320 - 446 °F | Membranes |
Lucobit Lucofin® 1414-t2 Polyolefin TPO Granules, Silk Grey Lucofin are colored, highly stabilized polyolefin-based TPO granules. The t2 series is distinguished by good tenacity, high biaxial extensibility and flexibility outstanding breaking strength, and .. |
|||
Processing Temperature | 160 - 302 °C | 320 - 576 °F | Extrusion |
Dyna-Purge® X Purging Compound Designed for Sheet & Profile ExtrusionGeneral Description:DYNA-PURGE X is a non-abrasive, non-chemical “engineered†thermoplastic purging compound, formulated to have a natural flow throug.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
Sumitomo Bakelite North America 2-530 Short-Glass Reinforced Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bakelite Nor.. |
|||
Processing Temperature | 160 - 220 °C | 320 - 428 °F | |
Total LDPE 1700 MN 18 C Low Density Polyethylene - Injection Molding and Compounding LDPE 1700 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant. Grade for easy flow injection molding of flexible parts, powder production for grindin.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | Glue Line Temperature |
EMS-Griltech Griltex® D 1309E Copolyester Hotmelt Adhesive (Apparel Interlinings) Description: GRILTEX adhesive products, either in pellet or powdered form, are used to coat apparel interlining substrates. Interlining substrates, coated with GRILTEX adhesive products, provides fo.. |
|||
Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
Daikin DAI-EL G-801 Fluoroelastomer Copolymer, Peroxide Curable Grade, 66% Fluorine Content Offers excellent chemical and steam resistance. Offers good mechanical characteristics.Features: Good low-temperature and elasticity characteristics.Information provided by Daikin Industries. |
|||
Processing Temperature | 160 - 175 °C | 320 - 347 °F | Plasticizing Zone |
Petroquimica Triunfo Trithene® TS 3003 LDPE - Film Grade The Trithene® TS 3003 resin is a low-density, high molecular weight polyethylene that offers high mechanical strength and excellent optical properties. The product shows high modulus of elasticity,.. |
|||
Processing Temperature | 160 °C | 320 °F | Suggested baking time at this temperature is 1.5 hr. |
Von Roll Isola IMI Varnish 707 Solventless Polyester Varnish for Electrical Insulation Data provided by Von Roll Isola USA.IMI solventless resins provide relatively void-free insulation for greater protection against severe environments and corona breakdown. Flash Point: 46°C. Usag.. |
|||
Processing Temperature | 160 °C | 320 °F | Suggested baking time at this temperature is 1.5 hr. |
Von Roll Isola IMI Varnish 777 Solventless Polyester Varnish for Electrical Insulation Data provided by Von Roll Isola USA.IMI solventless resins provide relatively void-free insulation for greater protection against severe environments and corona breakdown. Flash Point: 45°C. Usag.. |
|||
Processing Temperature | 160 - 180 °C | 320 - 356 °F | for 60-90 Shore A |
Kraiburg TPE THERMOLAST® K TP9CDB Natural Extrusion TPE with Adhesion to PP
(Unverified Data**) Standard natural compound for extrusionSubstitute for PVC-PTypical Applications: Seals and sealing profiles for windows and doors (black and colored)Coextrusion (hard/soft combinations)Material Adva.. |
|||
Processing Temperature | 160 - 200 °C | 320 - 392 °F | adhesion to engineering thermoplastics |
Kraiburg TPE THERMOLAST® K TP8NLZ Thermoplastic Elastomer, Adhesion to SAN, ASA, PMMA
(Unverified Data**) Typical Markets / Application Sectors:Industrial AppliancesElectrics & ElectronicsConsumer ElectronicsApplication Examples:SealsCoveringsDesign and functional elementsHandlesFunctional elementsAir i.. |
|||
Processing Temperature | 160 - 200 °C | 320 - 392 °F | Profiles and hoses |
Lucobit Lucofin® 1400HN Ethylene Butyl Acrylate Lucofin 1400HN is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin 1400HN is softer and more flexible than ethylene homopolym.. |
|||
Processing Temperature | 160 - 270 °C | 320 - 518 °F | Coatings |
Lucobit Lucofin® 1400HN Ethylene Butyl Acrylate Lucofin 1400HN is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin 1400HN is softer and more flexible than ethylene homopolym.. |
|||
Processing Temperature | 160 - 270 °C | 320 - 518 °F | Coatings |
Lucobit Lucolit® 1310 Polyolefin TPO Granules, Grey Lucolit is a colored, highly stabilized, bitumen-free TPO raw material based on polyolefins. Lucolit products display excellent tear resistance, flexibility, and weathering resistance. Lucolit exhi.. |
|||
Processing Temperature | 160 - 210 °C | 320 - 410 °F | |
RTP Company RTP 1200-65D TFE 10 Polyurethane Thermoplastic Elastomer (TPU) PTFE 10% - 65 Shore D
&am PTFE 10% - 65 Shore DComments:PTFE Lubricated65-D DurometerUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided .. |
|||
Processing Temperature | 160 - 210 °C | 320 - 410 °F | |
RTP Company RTP 1205-70D TFE 20 Polyurethane Thermoplastic Elastomer (TPU) Glass Fiber 30% - PTFE 20% - 70 Shore D Glass Fiber 30% - PTFE 20% - 70 Shore DComments:Glass FiberPTFE Lubricated70-D DurometerUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect pro.. |
|||
Processing Temperature | 160 - 210 °C | 320 - 410 °F | |
RTP Company ESD C 1200-80A Polyurethane Elastomer (TPU) Conductive - 80 Shore A
(discontin Conductive - 80 Shore AComments:ConductiveESD Protection80-A DurometerUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Informatio.. |
|||
Processing Temperature | 160 - 270 °C | 320 - 518 °F | Coatings |
Lucobit Lucofin® 1414-t3 Polyolefin TPO Granules, Silk Grey Lucofin are colored, highly stabilized polyolefin-based TPO granules. The t3 series is distinguished by good tenacity, high biaxial extensibility and flexibility outstanding breaking strength, and .. |