Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 124 - 300 MPa | 18000 - 43500 psi | Average value: 197 MPa Grade Count:47 |
Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an.. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP UX06002 PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UX06002 is a compound based on Polyphthalamide resin containing Aramide Fiber, PTFE. Added features include: Easy Molding, Internally Lubricated, Heat Stabilized. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM D9065 PEI Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON ZEF061XC PPO (Europe-Africa-Middle East) LNP* STATKON* ZEF061XC is a compound based on Polyphenyleneoxide resin containing Glass Fiber, Milled Carbon Fiber and Flame Retardant. Added Features include: Electrically Conductive |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Techmer ES Luriblend® HTN 01420 BK Availability: North AmericaForms: PelletsAdditive: Molybdenum Disulfide LubricantFeatures: Good Wear Resistance, Low Friction, High Heat Resistance and LubricatedAppearance: BlackInformation provide.. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Techmer ES Plastiblend® PA6/6 HS L N Nylon 66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and Nucleating AgentFeatures: Heat Stabilized, Impact Modified and NucleatedProcessing Method: Injection MoldingIn.. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Sumitomo Bakelite Durez® 23570 Phenolic, Compression Grade Durez 23570 Black Phenolic is a glass and mineral filled two-stage, special purpose molding material. It is designed for high strength, good dimensional stability, and electrical properties even aft.. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Sumitomo Bakelite North America 2008A Glass Reinforced Hardware Grade Epoxy Epoxy is the premier material for military firewall connectors.Information provided by Sumitomo Bak North America, Inc. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Clariant PA213M40 Nylon 6, 40% Mineral Reinforced, Heat Stabilized Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Clariant PA213M40BK Nylon 6, 40% Mineral Reinforced, Heat Stabilized, Black Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Clariant Renol 60G13HSP Black Nylon 6, 13% Glass Fiber Reinforced, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Clariant Renol PA101F/ST801 Nylon 66, Impact Modified, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Chem Polymer Chemlon 218 GV Nylon 6, 18% Glass Reinforced A flame retardant, glass reinforced grade of nylon 6. The material is UL94 V0 rated, completely non-halogenated and phosphorus free. It gives excellent surface appearance and is available in a ran.. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Chem Polymer Durlex 715 G PBT, 15% Glass Reinforced A lubricated, 15% glass reinforced PBT offering a balance of rigidity, dimensional stability and toughness.Data provided by the manufacturer, Chem Polymer. |
|||
Flexural Yield Strength | 124 - 152 MPa | 18000 - 22000 psi | |
Bulk Molding Compounds BMC A50-XHS Bulk molding compound Description: BMC A50XHS is a high strength bulk molding compound. It can be supplied in bulk or extruded in preweighted slugs. Due to the excellent flow and controlled reactivity, BMC A50XHS i.. |
|||
Flexural Yield Strength | 124 - 152 MPa | 18000 - 22000 psi | |
Bulk Molding Compounds BMC A50-XHS-U Bulk molding compound Description: BMC A50-XHS-U is a high strength bulk molding compound with a UL F1 rating for outdoor exposure. This material was specifically designed for outdoor lighting and electrical applications.. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Chem Polymer Chemlon 104-13 G Nylon 66, 13% Glass Fiber Reinforced A toughened, 13% glass fiber reinforced nylon 66 exhibiting improved toughness and ductility, especially dry as molded.Data provided by the manufacturer, Chem Polymer. |
|||
Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
Techmer ES HiFill® TPX-HTN-01043 A Availability: North AmericaForms: PelletsAdditive: Impact Modifier and LubricantFeatures: High Temperature Strength, Impact Modified and LubricatedUL File Number: E157318Information provided by TP C.. |