Polymer Property : Tensile Strength, Ultimate = 75.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 75.0 - 193 MPa
10900 - 28000 psi
Average value: 93.5 MPa Grade Count:13
Overview of materials for Polyetheretherketone, PEEK, Aramid Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PEEK, Aramid Fiber Filled". Each property range of values reported is minimum and ..
Tensile Strength, Ultimate 75.0 MPa
10900 psi
Polycasa Acryl® G 88 E Acrylic
Same as Lucryl G 88, but higher resistance to stress cracking and higher processing viscosity. Used for: extruded protective layer on PVC, ABS and PC for outdoor applications, as well as bath tubs ..
Tensile Strength, Ultimate 75.0 - 290 MPa
10900 - 42000 psi
Average value: 188 MPa Grade Count:7
Overview of materials for Phenolic/Glass Fiber SMC
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Glass Fiber SMC". Each property range of values reported is minimum and maximum values of appro..
Tensile Strength, Ultimate 75.0 - 353.701 MPa

@Temperature -40.0 - 150 °C
10900 - 51300.1 psi

@Temperature -40.0 - 302 °F
Average value: 147 MPa Grade Count:4
Overview of materials for Nylon 66, 60% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. ..
Tensile Strength, Ultimate 75.0 - 320 MPa
10900 - 46400 psi
Average value: 179 MPa Grade Count:43
Overview of materials for Nylon 66, 10% Carbon Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Carbon Fiber Filled". Specific grades with carbon fiber content between 5% and 14% are inc..
Tensile Strength, Ultimate 75.0 - 222 MPa
10900 - 32200 psi
Average value: 145 MPa Grade Count:80
Overview of materials for Nylon 610, Glass Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Glass Reinforced". Each property range of values reported is minimum and maximum values of ap..
Tensile Strength, Ultimate 75.0 MPa

@Temperature 22.0 °C
10900 psi

@Temperature 71.6 °F
25mm flat samples, compression moulded; ISO 527-4
Menzolit Menzolit® SMC 2600 Unsaturated Polyester UP
SMC 2600 is a special SMC with electrically conductive properties. Because of its conductivity, SMC 2600 is antistatic and prevents build-up of electrical charges on the surface. Despite of its cond..
Tensile Strength, Ultimate 75.0 MPa

@Temperature 1093 °C
10900 psi

@Temperature 1999 °F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Ultimate 75.0 MPa

@Temperature 22.0 °C
10900 psi

@Temperature 71.6 °F
25mm flat samples, compression moulded; ISO 527-4
Menzolit Menzolit® SMC 0420 Unsaturated Polyester UP
SMC 0420 is a low density Premium Class-A SMC for exterior body applications on cars, LCV´s and trucks. These compounds mould to light weight parts with good up to excellent surface quality for ..
Tensile Strength, Ultimate 75.0 MPa

@Temperature 22.0 °C
10900 psi

@Temperature 71.6 °F
25mm flat samples, compression moulded; ISO 527-4
Menzolit Menzolit® SMC 0421 Unsaturated Polyester UP
SMC 0421 is a low density premium Class-A SMC for on-line painted exterior body applications on cars. These compounds mould to light weight parts with excellent surface quality for on-line painted ..
Tensile Strength, Ultimate 75.0 MPa
10900 psi
Sapco C 220 Steatite
Information provided by Sapco.
Tensile Strength, Ultimate 75.0 MPa
10900 psi
Sapco C 221 Steatite
Information provided by Sapco.
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ISO 527
Wellman Wellamid® 42LH XE-N Unfilled Nylon 6, Lubricated & Heat Stabilized
Typical Applications: Automotive seat belt, buckle and anchor components; convoluted tubing for wire harnesses; furniture hardware, curtain glides.Data provided by the manufacturer, Wellman Inc.
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ISO 527
Wellman Wellamid® GS40-66 22L-N 40% Glass Sphere Filled Nylon 66, Lubricated
Typical Applications: Potentiometer liners, electrical coil forms, automotive window lift and power door lock switch bodies, gears, thick wall section moldings, emission control valves.Data provided..
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ISO 527
Wellman Wellamid® MR259 22LH-N 25% Mineral Reinforced Nylon 66, Lubricated & Heat Stabilized
Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co..
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ISO 527
Wellman Wellamid® T423-BK10 Mineral Reinforced Nylon 6, Heat Stabilized
Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co..
Tensile Strength, Ultimate 75.0 - 97.0 MPa
10900 - 14100 psi
ASTM D638
Zeus PEEK Tubing
PEEK (polyetheretherketone) is a high-performance engineered polymer with excellent endurance to heat and one of the highest strength-to-weight ratios of any thermoplastic. This material can be used..
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ASTM D638
Covestro Bayblend® T 88-4N Polycarbonate/ABS Blend, 20% Glass Fiber
Contains 20% glass fiber reinforcement, high stiffness.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – ..
Tensile Strength, Ultimate 75.0 MPa

@Temperature 180 °C
10900 psi

@Temperature 356 °F
ISO 527-1/-2
DSM Stanyl® OCD2100 BK27021 PA46-GF40
40% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate 75.0 MPa

@Temperature 180 °C
10900 psi

@Temperature 356 °F
ISO 527-1/-2
DSM Stanyl® OCD2300 BLK PA46-GF50
50% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate 75.0 MPa
10900 psi
BASF Luranyl® KR 2454/3 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced
Heat resistant grade with halogen-free flame retardant; applications include TV plug connectors and components in switchgear cabinets.Data was collected by ISO methods and provided by BASF.
Tensile Strength, Ultimate 75.0 MPa
10900 psi
BASF Procom® GC40S 402 Polypropylene
Uses: Electrical appliance housings (e.g. drills), components requiring high impact and temperature resistance, furniture frames.Data was collected by ISO methods and provided by BASF.
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ATSM D638
Ashley Polymers Ashlene® 630 Nylon 6, General Purpose
A general purpose Nylon 6 resin for injection molding.Data provided by the manufacturer
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ISO R527
Arkema Group Orgalloy® RS 6015 ES T6L Polyamide Alloy
Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group
Tensile Strength, Ultimate 75.0 MPa
10900 psi
BASF Luranyl® KR 2403 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced
General-purpose grade with 10% glass fiber for parts requiring especially good resistance to heat deformation.Applications: auto parts, steering-column cladding and water meters.Data was collected b..
Tensile Strength, Ultimate 75.0 - 110 MPa
10900 - 16000 psi
Average value: 88.0 MPa Grade Count:5
Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled". Each property range of values reported is ..
Tensile Strength, Ultimate 75.0 - 150 MPa
10900 - 21800 psi
Average value: 102 MPa Grade Count:29
Overview of materials for Polyethylene Terephthalate (PET), 20% Glass Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 20% Glass Reinforced". Specific grades with glass content between 15% ..
Tensile Strength, Ultimate 75.0 MPa
10900 psi
5 mm/min; ISO 527
Lucite International Perspex™ GS Acrylic Cast Sheet 000/0000
PERSPEX cast sheet is made between sheets of high quality glass and produced in batches. It has a very high molecular weight making it strong, resilient and easy to handle and fabricate. The cast me..
Tensile Strength, Ultimate 75.0 - 105 MPa
10900 - 15200 psi
ASTM D638-68
Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black  (discontinued **)
Used for parts requiring high strength at room temperature, good retention of properties at high temperatures and corrosion resistance, such as diesel engine external body parts.Data provided by the..
Tensile Strength, Ultimate 75.0 - 88.0 MPa
10900 - 12800 psi
Average value: 82.3 MPa Grade Count:3
Overview of materials for Thermoset Polyurethane, Liquid, Quartz Filled
This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid, Quartz Filled". Each property range of values reported is minimum and ma..
Copyright © lookpolymers.com All Rights Reserved