Shell Carilon® D26VM100 Polyketone, High-Flow Injection Molding Grade  (discontinued **)

Category Polymer , Thermoplastic , Polyketone
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Shell Carilon® D26VM100 Polyketone, High-Flow Injection Molding Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26VM100 is a high-flow injection molding grade with mechanical properties which classify it as an engineering thermoplastic. This grade exhibits very good processability, good impact resistance, high resilience and good creep performance. CARILON Polymer D26VM100 can also withstand short-term exposure to elevated temperatures. Moreover this polymer exhibits a high resistance to hydrocarbons, solvents, salt solutions, weak acids and weak bases. CARILON Polymer D26VM100 is a high-flow, low-viscosity polymer that should be considered for moldings with long flow paths or thin walls. This grade is very easy to process on standard injection molding equipment. Cycle times are generally short. Parts show good mold definition with glossy mar-resistant surfaces. CARILON Polymers' low moisture sensitivity means that no conditioning of parts before assembly or use is necessary.Data provided by Shell Chemical.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Water Absorption 0.45 %
0.45 %
24 hour immersion; ASTM D570
Moisture Absorption at Equilibrium 0.50 %
0.50 %
at 50% RH at Equilibrium; ASTM D570
Water Absorption at Saturation 2.2 %
2.2 %
at saturation; ASTM D570
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
ASTM D955
Melt Flow 60 g/10 min

@Load 2.16 kg,
Temperature 240 °C
60 g/10 min

@Load 4.76 lb,
Temperature 464 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Hardness, Shore D 77
77
ISO 868
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
ASTM D638
Elongation at Break >= 250 %
>= 250 %
ASTM D638
Elongation at Yield 20 %
20 %
ASTM D638
Tensile Modulus 1.50 GPa
218 ksi
ASTM D638
Flexural Strength 59.0 MPa
8560 psi
at 5% strain; ASTM D790
Flexural Modulus 1.50 GPa
218 ksi
ASTM D790
Izod Impact, Notched 0.950 J/cm
1.78 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Gardner Impact >= 45.0 J
>= 33.2 ft-lb
Thermal Properties Metric English Comments
CTE, linear 110 µm/m-°C

@Temperature 25.0 - 55.0 °C
61.1 µin/in-°F

@Temperature 77.0 - 131 °F
ASTM E831
Melting Point 220 °C
428 °F
Deflection Temperature at 0.46 MPa (66 psi) 203 °C
397 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ASTM D648
Flammability, UL94 HB
HB
Oxygen Index 22 %
22 %
ISO 4589
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257
Dielectric Constant 5.3

@Frequency 1e+6 Hz
5.3

@Frequency 1e+6 Hz
ASTM D150
6.0

@Frequency 1000 Hz
6.0

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 18.0 kV/mm

@Thickness 1.60 mm
457 kV/in

@Thickness 0.0630 in
Short Term; ASTM D149
Dissipation Factor 0.010

@Frequency 1000 Hz
0.010

@Frequency 1000 Hz
ASTM D150
0.050

@Frequency 1e+6 Hz
0.050

@Frequency 1e+6 Hz
ASTM D150
Comparative Tracking Index 600 V
600 V
UL746A