SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer + Glass/PTFE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KFL36 is an Acetal containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.75 g/cc
1.75 g/cc
ASTM D 792
Density 1.75 g/cc
0.0632 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.26 %
0.26 %
23°C / 50% RH; ISO 62
0.16 %

@Time 86400 sec
 0.16 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0070 - 0.010 cm/cm

@Time 86400 sec
 0.0070 - 0.010 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 84.0 MPa
12200 psi
5 mm/min; ISO 527
88.0 MPa
12800 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 84.0 MPa
12200 psi
5 mm/min; ISO 527
88.0 MPa
12800 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 1.3 %
1.3 %
Type I, 5 mm/min; ASTM D 638
1.3 %
1.3 %
5 mm/min; ISO 527
Elongation at Yield 1.3 %
1.3 %
Type I, 5 mm/min; ASTM D 638
1.3 %
1.3 %
5 mm/min; ISO 527
Tensile Modulus 10.61 GPa
1539 ksi
1 mm/min; ISO 527
10.82 GPa
1569 ksi
50 mm/min; ASTM D 638
Flexural Strength 107 MPa
15500 psi
1.3 mm/min, 50 mm span; ASTM D 790
130 MPa
18900 psi
ISO 178
Flexural Modulus 9.28 GPa
1350 ksi
1.3 mm/min, 50 mm span; ASTM D 790
9.93 GPa
1440 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.500 J/cm

@Temperature 23.0 °C
 0.937 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 3.26 J/cm

@Temperature 23.0 °C
 6.11 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
10.0 J

@Temperature 23.0 °C
 7.38 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.40
0.40
ASTM D 3702 Modified
Coefficient of Friction, Static 0.46
0.46
ASTM D 3702 Modified
K (wear) Factor 473 x 10-8 mm³/N-M
235 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 52.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 65.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 36.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
183 °C

@Thickness 3.20 mm
 361 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 161 °C
322 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
161 °C

@Thickness 3.20 mm
 322 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Users viewing this material also viewed the following: