Samsung Cheil Industries Infino® EF-1032 PC/ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Samsung Cheil Industries Infino® EF-1032 PC/ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion resin, non-halogen flame-retardantInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0050 - 0.0070 in/in <br>@Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 19 g/10 min <br>@Load 10.0 kg,<br> Temperature 250 °C |
19 g/10 min <br>@Load 22.0 lb,<br> Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 68.6 MPa | 9950 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 61.8 MPa | 8960 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 120 % | 120 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.26 GPa | 327 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 88.3 MPa | 12800 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 4.22 J/cm <br>@Thickness 6.35 mm |
7.90 ft-lb/in <br>@Thickness 0.250 in |
ASTM D256 |
| 8.34 J/cm <br>@Thickness 3.17 mm |
15.6 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C <br>@Thickness 6.40 mm |
217 °F <br>@Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C <br>@Thickness 6.40 mm |
203 °F <br>@Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 107 °C | 225 °F | B/50; ISO R306 |
| 110 °C | 230 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-0 <br>@Thickness 1.50 mm |
V-0 <br>@Thickness 0.0591 in |
Users viewing this material also viewed the following:
- Kazanorgsintez 108-274 Thermostabilized Low Density Polyethylene Composition for Radiation Modification
- LyondellBasell Pro-fax SG702 Polypropylene Impact Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP WL0049 PBT (Europe-Africa-Middle East)
- Teknor Apex Beetle® 66GF6 Nylon 66, 30% Short Glass Fiber Reinforced
- Ensinger Tecapeek® XP-106 Compression Molded PEEK Compound, 40% Fiberglass
- Eurotec® Tecomid® NA40 GR30 NL RM PA 6.6 30% glass fiber reinforced, low friction and wear
- Beijing Chemical Industry KAIFA® 301-G30 PBT Resin
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 30A, Black Sulfur Cure
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved