SABIC Innovative Plastics NORYL PKN4775 PPE+PS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PKN4775 PPE+PS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPE+PS blend. Opaque. FDA compliant in limited colors. High heat. Modulus at elevated temperature. Good ESCR performance. Thin wall extrusion and injection molding. Typical applications include packaging for high performance applications.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Moisture Absorption 0.0500 %
0.0500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.25 %
0.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 15.3 g/10 min

@Load 5.00 kg,
Temperature 300 °C
15.3 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 14 g/10 min

@Load 5.00 kg,
Temperature 300 °C
14 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D638
47.0 MPa
6820 psi
50 mm/min; ISO 527
Tensile Strength, Yield 51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
51.0 MPa
7400 psi
50 mm/min; ISO 527
Elongation at Break 29.3 %
29.3 %
50 mm/min; ISO 527
35 %
35 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.1 %
4.1 %
50 mm/min; ISO 527
5.1 %
5.1 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.12 GPa
307 ksi
5 mm/min; ASTM D638
2.12 GPa
307 ksi
1 mm/min; ISO 527
Flexural Yield Strength 78.0 MPa
11300 psi
1.3 mm/min, 50 mm span; ASTM D790
82.0 MPa
11900 psi
2 mm/min; ISO 178
Flexural Modulus 2.16 GPa
313 ksi
2 mm/min; ISO 178
2.21 GPa
321 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.68 J/cm
5.02 ft-lb/in
ASTM D256
1.61 J/cm

@Temperature -30.0 °C
3.02 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.90 J/cm²
9.04 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 39.0 J

@Temperature 23.0 °C
28.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 92.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
92.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 138 °C

@Thickness 3.20 mm
280 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
122 °C

@Thickness 3.20 mm
252 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 142 °C
288 °F
Rate B/50; ASTM D1525
142 °C
288 °F
Rate B/50; ISO 306
144 °C
291 °F
Rate B/120; ISO 306