SABIC Innovative Plastics Lexan® FST9436 PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FST9436 PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium viscosity opaque, low smoke, and OSU 65/65 compliant PC Copolymer
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
44 g/10 min

@Load 5.00 kg,
Temperature 300 °C
44 g/10 min

@Load 11.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D638
58.0 MPa
8410 psi
50 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
65.0 MPa
9430 psi
50 mm/min; ISO 527
Elongation at Break 92 %
92 %
50 mm/min; ISO 527
103 %
103 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.3 %
6.3 %
50 mm/min; ISO 527
6.5 %
6.5 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.26 GPa
328 ksi
5 mm/min; ASTM D638
2.26 GPa
328 ksi
1 mm/min; ISO 527
Flexural Yield Strength 96.0 MPa
13900 psi
2 mm/min; ISO 178
102 MPa
14800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.28 GPa
331 ksi
2 mm/min; ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 4.11 J/cm
7.70 ft-lb/in
ASTM D256
1.23 J/cm

@Temperature -30.0 °C
2.30 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 22.0 kJ/m²
10.5 ft-lb/in²
80*10*4; ISO 180/1A
13.0 kJ/m²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.70 J/cm²
12.8 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 74.0 J

@Temperature 23.0 °C
54.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Hot Ball Pressure Test <= 125 °C
<= 257 °F
IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
134 °C

@Thickness 3.20 mm
273 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 152 °C
306 °F
Rate B/50; ISO 306
154 °C
309 °F
Rate B/50; ASTM D1525
154 °C
309 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
NBS Smoke Density, Flaming, Dmax <40
ASTM E 662
OSU total heat release (2 minute test) <65kW-min/m^2
FAR 25.853
OSU peak heat release rate (5 minute test) <65kW/m^2
FAR 25.853
Vertical Burn a (60s) passes at <15sec
FAR 25.853
Vertical Burn b (12s) passes at <15sec
FAR 25.853