SABIC Innovative Plastics LNP Verton RV006ESV_GY7E071 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton RV006ESV_GY7E071 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary Data for 30% long glass fiber, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
1.389 g/cc
0.05018 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 1.2 %
1.2 %
23°C / 50% RH; ISO 62
0.66 %

@Time 86400 sec
0.66 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0029 - 0.0049 cm/cm

@Time 86400 sec
0.0029 - 0.0049 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 161 MPa
23400 psi
Type I, 5 mm/min; ASTM D 638
163 MPa
23600 psi
5 mm/min; ISO 527
Tensile Strength, Yield 162 MPa
23500 psi
Type I, 5 mm/min; ASTM D 638
163 MPa
23600 psi
5 mm/min; ISO 527
Elongation at Break 2.3 %
2.3 %
Type I, 5 mm/min; ASTM D 638
2.3 %
2.3 %
5 mm/min; ISO 527
Elongation at Yield 2.3 %
2.3 %
Type I, 5 mm/min; ASTM D 638
2.3 %
2.3 %
5 mm/min; ISO 527
Tensile Modulus 8.32 GPa
1210 ksi
1 mm/min; ISO 527
9.11 GPa
1320 ksi
50 mm/min; ASTM D 638
Flexural Strength 228 MPa
33100 psi
2 mm/min; ISO 178
234 MPa
33900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 7.75 GPa
1120 ksi
2 mm/min; ISO 178
8.65 GPa
1250 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.520 J/cm

@Temperature -40.0 °C
0.974 ft-lb/in

@Temperature -40.0 °F
ASTM D 256
0.570 J/cm

@Temperature 23.0 °C
1.07 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 9.38 J/cm

@Temperature 23.0 °C
17.6 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
14.0 kJ/m²

@Temperature -40.0 °C
6.66 ft-lb/in²

@Temperature -40.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 52.0 kJ/m²

@Temperature -40.0 °C
24.7 ft-lb/in²

@Temperature -40.0 °F
80*10*4; ISO 180/1U
158 kJ/m²

@Temperature 23.0 °C
75.2 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 7.00 J

@Temperature 23.0 °C
5.16 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
12.0 J

@Temperature 23.0 °C
8.85 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 33.7 µm/m-°C

@Temperature -30.0 - 30.0 °C
18.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM E 831
CTE, linear, Transverse to Flow 63.5 µm/m-°C

@Temperature -30.0 - 30.0 °C
35.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 261 °C
502 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
260 °C

@Thickness 3.20 mm
500 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 256 °C
493 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
256 °C

@Thickness 3.20 mm
493 °F

@Thickness 0.126 in
unannealed; ASTM D 648