Resinoid 7051 Phenolic Molding, Glass Reinforced

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer Resinoid
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinoid 7051 Phenolic Molding, Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ASTM D792A
Water Absorption 0.10 %
0.10 %
24 hours R.T. ASTM D570
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
Positive Mold; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell E 100
100
ASTM D785
Hardness, Rockwell M 120
120
ASTM D785
Tensile Strength, Ultimate 65.0 MPa
9430 psi
ASTM D651
Flexural Strength 165 MPa
23900 psi
ASTM D790
Flexural Modulus 17.0 GPa
2470 ksi
ASTM D790
Compressive Strength 276 MPa
40000 psi
ASTM D695
Izod Impact, Notched 0.473 J/cm
0.886 ft-lb/in
ASTM D256A
Thermal Properties Metric English Comments
CTE, linear 38.0 µm/m-°C

@Temperature 20.0 °C
21.1 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Maximum Service Temperature, Air 150 °C
302 °F
UL RTI
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ASTM D648
UL RTI, Electrical 150 °C
302 °F
UL RTI, Mechanical with Impact 150 °C
302 °F
UL RTI, Mechanical without Impact 150 °C
302 °F
Electrical Properties Metric English Comments
Dielectric Strength 14.6 kV/mm
371 kV/in
Short Time; Dry; ASTM D149
Arc Resistance 180 sec
180 sec
ASTM D495
Comparative Tracking Index 175 - 250 V

@Thickness 3.05 mm
175 - 250 V

@Thickness 0.120 in
UL PLC 3 (175-250 V)
Hot Wire Ignition, HWI >= 0.00 sec

@Thickness 3.05 mm
>= 0.00 sec

@Thickness 0.120 in
UL PLC 0
High Amp Arc Ignition, HAI 15 - 29 arcs

@Thickness 3.05 mm
15 - 29 arcs

@Thickness 0.120 in
UL PLC 3, 15-29 arcs
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min

@Thickness 3.05 mm
0.000 - 0.394 in/min

@Thickness 0.120 in
UL PLC 0 (0-10 mm/min)
Processing Properties Metric English Comments
Mold Temperature 155 - 180 °C
311 - 356 °F