Polymer Property : Tensile Strength at Break = 163 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 163 MPa
23600 psi
ASTM D638
LNP Lubricomp® PDX-U-95672 BK8-115 Polyphthalamide, Proprietary Filler  (discontinued **)
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Tensile Strength at Break 163 MPa
23600 psi
Type I, 5 mm/min; ASTM D638
LNP ULTEM® EXCP0096 Polyetherimide, 30% Carbon Fiber Reinforcement, 10% PTFE Lubricant  (discontinued **)
Features: Lubricated, Electrically Conductive, Good Wear Resistance, High Heat ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This dat..
Tensile Strength at Break 163 MPa
23600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear (Europe-Africa-Middle East)
LNP* Lubricomp* OCL4036L is a compound based on PPS - Linear resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 163 MPa
23600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCL36XXP PPS - Linear (Europe-Africa-Middle East)
LNP* LUBRICOMP* OCL36XXP is a compound based on PPS- Linear resin containing PTFE, Carbon Fiber. Added features include : Internally Lubricated, Electrically Conductive .
Tensile Strength at Break 163 MPa
23600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66
LNP LUBRICOMP* RX06480 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% Lubricants. Added feature of this material is: Wear Resistant.
Tensile Strength at Break 163 MPa
23600 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP UX95672 PPA
LNP LUBRICOMP* UX95672 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Tensile Strength at Break 163 MPa
23600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON JX89626 PES
LNP* STAT-KON* JX89626 is a compound based on Polyethersulfone containing Proprietary Fillers. Added feature of this material is: Electrically Conductive.
Tensile Strength at Break 163 MPa
23600 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LC003E PEEK
LNP THERMOCOMP* LC003E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive
Tensile Strength at Break 163 MPa
23600 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LC003E PEEK (Asia Pacific)
LNP THERMOCOMP* LC003E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 163 MPa
23600 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66
LNP* Thermocomp* RF-1006 EP HS is based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade include Exceptional Processing and Heat Stabilizer.This data was supplied by SABIC-IP for ..
Tensile Strength at Break 163 MPa
23600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON OE004AE PPS - Branched
LNP STAT-KON* OE004AE is a compound based on PPS - Branched resin containing 20% Carbon Fiber. Added features of this material are: Easy Molding, Electrically Conductive.
Tensile Strength at Break 163 MPa
23600 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PX87791 PA 6
LNP* THERMOCOMP* PX87791 is a compound based on Nylon 6 resin containing Proprietary Filler(s).
Tensile Strength at Break 163 MPa

@Temperature -40.0 °C
23600 psi

@Temperature -40.0 °F
ISO Data
BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Dry)
Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade.
Tensile Strength at Break 163 MPa
23600 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Verton RV006ESV_GY7E071 PA 66
Preliminary Data for 30% long glass fiber, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 163 MPa

@Temperature 23.0 °C
23600 psi

@Temperature 73.4 °F
DAM; ISO 527
DuPont Performance Polymers Zytel® 73G30TGI BK267 Nylon 6  (Unverified Data**)
Zytel® 73G30TGI BK267 is a 30% glass fiber reinforced, toughened, black polyamide 6 optimized for gas injection molding process.Information provided by DuPont Performance Polymers
Tensile Strength at Break 163 MPa
23600 psi
ISO 527
SABIC Innovative Plastics LNP Verton WV00A PBT (Europe-Africa-Middle East)
LNP VERTON* WV00A is a compound based on Polybutylene Terephalate resin containing Long Glass.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.