SABIC Innovative Plastics LNP THERMOCOMP WH0200B PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WH0200B PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* WH0200B is a compound based on PBT resin containing proprietary fillers. Added features include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.05 g/cc | 2.05 g/cc | ASTM D792 |
| Density | 2.044 g/cc | 0.07384 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| 1.5 % | 1.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.02 GPa | 873 ksi | 1 mm/min; ISO 527 |
| 6.23 GPa | 904 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.41 GPa | 785 ksi | 2 mm/min; ISO 178 |
| 5.45 GPa | 790 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.47 J/cm | 4.63 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ X ST6600-0041 ES NHFR Black Polyamide 66 (Nylon 66)
- Niche Polymer PA66GF43N Nylon 66, 43% Glass Fiber Filled
- Parker Chomerics CHO-FLEX 602 Conductive Coating
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR N550 (FEF) Filler
- Stir SpA AF 89 CZ (PVC)
- Total 2285 HDPE Bimodal Film Resin
- Lubrizol ESTALOC® 59300 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane
- EMS-Grivory Grivory® BGZ-15 PA6-GF15
- SABIC Innovative Plastics NORYL FR9310 PPE (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved