- HOME
- POLYMER SEARCH
- Polymer Property : Flexural Strength = 84.0 MPa
Polymer Property : Flexural Strength = 84.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | <= 84.0 MPa | <= 12200 psi | ISO 178 |
| Polykemi AB POLYblend 45FS GKF2010 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| SABIC Innovative Plastics Lexan® LCR200 PBT+PC (Asia Pacific) |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| PolyOne Geon™ Vinyl Dry Blend E7009 Polyvinyl Chloride, Rigid (PVC, Rigid) Recommended for whites and light pastel colors only. Not to be used for darker colors.Physical properties based on Geon E7009 white 1024 lot# UTCX 57572Information provided by PolyOne |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP BX03658N SAN LNP* LUBRICOMP* BX03658N is a compound based on SAN resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Tight Dimensional Tolerances, good for Water Meter A.. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DAL22 PC (Asia Pacific) LNP* Lubricomp* DAL22 is a compound based on Polycarbonate resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DL003 PC (Europe-Africa-Middle East) LNP* Lubricomp* DL003 is a compound based on Polycarbonate resin containing PTFE. |
|||
| Flexural Strength | <= 84.0 MPa | <= 12200 psi | ISO 178 |
| Polykemi AB POLYabs HD2 ABS Information provided by Polykemi AB |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Kotec Carbotex K-30F5 Polycarbonate, Wear Resistant Features: Wear resistance, TranslucentApplications: OA equipment, Communications, Precision parts, Machineries, E & E partsInformation provided by Kotec Corporation |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Kotec Carbotex K-30FR Polycarbonate, Flame Retardant Features: Non-brominated & non-chlorined flame retardant, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, E & E parts, Safety products, Househo.. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Kotec Carbotex K-30FRT12 Polycarbonate, Flame Retardant Features: Non-brominated & non-chlorined flame retardant, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, E & E parts, Safety products, Househo.. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Kotec Carbotex KFR-30 Polycarbonate, Flame Retardant Features: Non-brominated & non-chlorined flame retardant, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, E & E parts, Safety products, Househo.. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Gromax CCP PBT 1100-600S Product Description: PBT unreinforced high viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Excell.. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DL003E PC (Asia Pacific) LNP LUBRICOMP* DL003E is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Easy Molding. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP IBI16 PA 6/12 LNP LUBRICOMP* IBI16 is a compound based on Nylon 6/12 resin containing 30% Glass Bead, 2% Silicone. Added features of this material include: Wear Resistant. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1000 PC (Asia Pacific) |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66 LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRILOY K2000XXH Acetal LNP LUBRILOY* K2000XXH is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material are: Wear Resistant, Healthcare. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Stat-kon DX07323 PC+ABS LNP* STAT-KON* DX07323 is a compound based on polycarbonate resin containing conductive fillers. Added features of this compound includes: ESD safe and excellent low-temperature impact performance, .. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON DX93500 PC LNP STAT-KON* DX93500 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D 790 |
| SABIC Innovative Plastics Valox® VAC3001 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS LNP* STAT-LOY* N30009 is a compound based on PC+ABS Blend resin. Added features of this material include: Antistat, Flame Retardant. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY NX03583 PC+ABS LNP STAT-LOY* NX03583 is a compound based on PC+ABS Blend resin. Added features of this material include: Antistat, Flame Retardant. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Plenco 00714 Melamine-Phenolic, Granular, Compression Molded PLENCO 00714 is a melamine-phenolic copolymer molding compound, offering excellent arc resistance and comparative track index values. Type ASTM D 5948 CMG, and UL recognized under component file E4.. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Plenco 3509 Phenolic, Granular, Injection Molded PLENCO 03509 is a mineral and flock filled phenolic molding compound offering excellent electrical properties, dimensional stability, and improved heat resistance. UL recognized under component file.. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| Polyplastics Duracon® ES-5 Acetal Co-polymer (POM), Conductive, Antistatic DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DL003E PC LNP LUBRICOMP* DL003E is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Easy Molding, Internally Lubricated |
|||
| Flexural Strength | 84.0 MPa | 12200 psi | 2 mm/min; ISO 178 |
| Sax Polymers SAXALEN PPC344G25 Polypropylene Copolymer, 25% Glass Filled SAXALEN PPC344G25 is a 25% glass filled Polypropylene - Copolymer intended for injection molding.Information provided by SAX Polymers |
|||