- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 156 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 156 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer (Asia Pacific) XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer (Asia Pacific) XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer (Europe-Africa-Middle East) XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | As molded; ISO 75A-f |
| Victrex® PEEK 90G Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact c.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Lexan® EXRL0627 PC Copolymer EXRL0627 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and transparent colors.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 4.00 mm |
313 °F @Thickness 0.157 in |
after annealing 150°C 16 hr; ASTM D648 |
| Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound
(discontinued **) Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | |
| Lehmann & Voss LUVOCOM® 1105/BK7308-1 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Suitable for biocompatible application.Not f.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | |
| Lehmann & Voss LUVOCOM® 1105/GN7348 PEEK, unreinforced, laser markable Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High chemical resistance parts, non flammable.Not flammable.Especially suitable for medica.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl PX7446 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RAL22I PA 66 LNP* LUBRICOMP* RAL22I is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant, High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC STAMAX 20YK270 PP SABIC® STAMAX 20YK270 is a 20% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stif.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC STAMAX 30YM243 PP SABIC® STAMAX 30YM243 is a 30% long glass fiber reinforced UV stabilized polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMD.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 LNP* THERMOCOMP* PH0460A is a compound based on Nylon 6. Added feature of this material is: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Unannealed; ISO 75-2/A |
| Styron INSPIREâ„¢ DLGF 9621.00 Compounded Polypropylene, 60% LGF Overview: DLGF 9621.00 is a polypropylene homopolymer reinforced with 60% by weight of long glass fiber. PP-LGF60, Long Glassfiber Granulate). DLGF 9621.00 is produced by pultrusion/melt-impregnatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Unannealed; ISO 75-2/A |
| Styron LGF 9621 Homopolymer Polypropylene Overview: LGF 9621 is polypropylene homopolymer reinforced with 60% by weight of long glass fibers. (PP-LGF60, Long Glass fiber Granulate). This PP-LGF60 is a ‘concentrate’ which has to be.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOTUF MF0049I PP (Europe-Africa-Middle East) LNP* THERMOTUF* MF0049I is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features include; Flame Retardant, Chemically Coupled. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp LFZ42XXC PEEK LNP THERMOCOMP* LFZ42XXC is a compound based on Polyetheretherketone resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage.This data was supplied by SABIC.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp PFB42ES PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PFB42ES is a compound based on PA6 resin containing Glass Fiber, Glass Bead. Added features include: Easy Molding, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP VERTON MX02795 PP LNP* VERTON* MX02795 is a compound based on Polypropylene resin containing Proprietary Fillers. Added features of this material include: Heat Stabilized, UV Stabilized, Structural. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | ASTM D648 |
| Plenco 7100 Phenolic, Nodular, Injection Molded PLENCO 07100 is an organic fiber reinforced phenolic molding compound, with improved mechanical strength properties and an industrial finish. 07100 is densified for easy handling and good pourabilit.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Staramide PFB42ES PA6, Glass Fiber/Bead Filled, Injection Molded Starflam PFB42ES is a Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | ASTM D648 |
| Asahi Kasei Thermylene® P7-45FG-0790 45% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 (Asia Pacific) LNP* Thermocomp* PH0460A is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC STAMAX 20YM240 PP SABIC® STAMAX 20YM240 is a 20% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 62455287. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp PFB42EU PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PFB42EU is a compound based on PA 6 resin containing Glass Fiber, Glass Bead. Added features include Easy Molding, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-.. |
|||